Effect of silicon dioxide on the formation of the phase composition and pore structure of titanium dioxide with the anatase structure

被引:0
作者
G. A. Zenkovets
V. Yu. Gavrilov
A. A. Shutilov
S. V. Tsybulya
机构
[1] Russian Academy of Sciences,Boreskov Institute of Catalysis, Siberian Branch
来源
Kinetics and Catalysis | 2009年 / 50卷
关键词
Rutile; Anatase Phase; Tetraethyl Orthosilicate; Nanocrystalline Structure; Anatase Structure;
D O I
暂无
中图分类号
学科分类号
摘要
The formation of the structure of titanium dioxide modified with silicon dioxide, which was introduced as tetraethyl orthosilicate, was studied. It was found that the formation of the nanocrystalline structure of TiO2 occurred upon the modification of titanium dioxide with silicon dioxide. This nanocrystalline structure of TiO2 was formed by highly dispersed anatase particles of size 6–10 nm stabilized by silicon oxide layers, which were formed upon the decomposition of tetraethyl orthosilicate. An increase in the modifier concentration resulted in a deceleration of the growth of anatase particles and an increase in the temperature of the phase transition of anatase to rutile. It was found that the anatase phase in the samples containing 5–15 wt % SiO2 was stable up to 1000°C. The stabilization of highly dispersed anatase particles facilitated the retention of the developed fine-pore structure of xerogels with a pore diameter of 4 nm up to 900°C.
引用
收藏
页码:760 / 767
页数:7
相关论文
共 102 条
  • [1] Kryukova G.N.(2007)undefined Appl. Catal., B 71 169-undefined
  • [2] Zenkovets G.A.(1994)undefined Catal. Today 20 171-undefined
  • [3] Shutilov A.A.(2005)undefined J. Phys. Chem. B 109 23430-undefined
  • [4] Wilde M.(2000)undefined J. Phys. Chem. B 104 8989-undefined
  • [5] Gunter K.(1996)undefined J. Electrochem. Soc. 143 394-undefined
  • [6] Fassler D.(1993)undefined J. Mater. Chem. 12 1239-undefined
  • [7] Richter K.(1978)undefined J. Solid State Chem. 23 93-undefined
  • [8] Vedrine J.C.(2006)undefined Ceram. Int. 32 593-undefined
  • [9] Alexeev O.S.(1988)undefined Zh. Prikl. Khim. 61 3124-undefined
  • [10] Chin S.Y.(1964)undefined Lakokras. Mater. 2 2143-undefined