Oxidation Behavior of Silicon-Aluminizing Coating on ?-TiAl Alloy at Different Temperatures

被引:6
作者
Zhao, Feng [1 ,2 ]
Huang, Jiang [1 ,2 ]
Cui, Xinyu [1 ]
Wang, Jiqiang [1 ]
Xiong, Tianying [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
基金
中国国家自然科学基金;
关键词
gamma-TiAl; cold spray; high-temperature oxidation; silicon-aluminizing diffusion coating; Ti5Si3; AL-SI; RESISTANCE; IMPROVEMENT; MICROSTRUCTURE; 900-DEGREES-C; PROTECTION; MECHANISM;
D O I
10.1007/s11665-023-08275-9
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this research, a silicon-aluminizing diffusion coating constituted of homogenous Ti(Al, Si)(3) phase was prepared on ?-TiAl alloy using cold spraying Al-40Si (wt.%) alloy coating followed by thermal diffusion treatment. The oxidation behavior of the diffusion coating was tested for 300 h at high temperatures of 900, 950 and 1000 degrees C. The differences in microstructure evolution at three different temperatures, as well as antioxidant properties of the coating, were investigated. The results showed that the weight gain of the coating after 300-h oxidation at 900, 950 and 1000 degrees C was sharply reduced to only 1.195, 1.550 and 1.925 mg cm(-2), respectively. Although the alumina-based oxide scale formed on the coating became thicker with the increasing oxidation temperature, it had a good adherence to the coating even at 1000 degrees C. Thus, the coating can significantly improve the oxidation resistance of the ?-TiAl alloy at three temperatures because the generated oxide scale can act as a barrier to prevent the outward diffusion of Ti and the internal diffusion of O. The degradation rate of the coating also increased with the increasing oxidation temperature. Following 300 h of oxidation test at 1000 degrees C, the homogenous Ti(Al, Si)(3) phase in the coating almost entirely degraded. However, the in situ formed Ti(5)Si(3 )diffusion layer maintained a good stability at 1000 degrees C, which can block the further invasion of O to a certain extent.
引用
收藏
页码:4447 / 4460
页数:14
相关论文
共 41 条
  • [1] Appel F, 2000, ADV ENG MATER, V2, P699, DOI 10.1002/1527-2648(200011)2:11<699::AID-ADEM699>3.0.CO
  • [2] 2-J
  • [3] Bonding mechanism in cold gas spraying
    Assadi, H
    Gärtner, F
    Stoltenhoff, T
    Kreye, H
    [J]. ACTA MATERIALIA, 2003, 51 (15) : 4379 - 4394
  • [4] Oxygen absorption and diffusion in Ti5Si3
    Bakulin, Alexander, V
    Chumakova, Lora S.
    Kulkova, Svetlana E.
    [J]. INTERMETALLICS, 2022, 146
  • [5] Aluminum diffusion inhibiting properties of Ti5Si3 at 900 °C and its beneficial properties on Al-rich oxidation protective coatings on γ-TiAl
    Bauer, Peter-Philipp
    Swadzba, Radoslaw
    Klamann, Lisa
    Laska, Nadine
    [J]. CORROSION SCIENCE, 2022, 201
  • [6] Increasing the oxidation resistance of γ-TiAl by applying a magnetron sputtered aluminum and silicon based coating
    Bauer, Peter-Philipp
    Laska, Nadine
    Swadzba, Radoslaw
    [J]. INTERMETALLICS, 2021, 133
  • [7] MECHANISM OF ISOTHERMAL OXIDATION OF THE INTERMETALLIC TIAL AND OF TIAL ALLOYS
    BECKER, S
    RAHMEL, A
    SCHORR, M
    SCHUTZE, M
    [J]. OXIDATION OF METALS, 1992, 38 (5-6): : 425 - 464
  • [8] Al-Si and Al-Si-Y coatings deposited by HS-PVD for the oxidation protection of γ-TiAl
    Bobzin, K.
    Broegelmann, T.
    Kalscheuer, C.
    Liang, T.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2018, 350 : 587 - 595
  • [9] The improvement of high temperature oxidation of Ti-50Al by sputtering Al film and subsequent interdiffusion treatment
    Chu, MS
    Wu, SK
    [J]. ACTA MATERIALIA, 2003, 51 (11) : 3109 - 3120
  • [10] Clemens H, 2000, ADV ENG MATER, V2, P551, DOI 10.1002/1527-2648(200009)2:9<551::AID-ADEM551>3.0.CO