Preparation of epoxy-based insulator and optimization of its thermal property by Taguchi robust design method in double base propellant grain application

Taguchi method (orthogonal array, OA9) was used to design an epoxy insulator by evaluating its glass transition temperature (Tg) for using in a double base (DB) propellant grain. In this design method, three epoxy resins based on diglycidylether bisphenol A (DGEBA), three polyamine curing agents and a DGEBA-based reactive diluent agent were used. The curing process of epoxy resins with polyamines was studied by Fourier transform infrared spectroscopy. The results showed that the curing process was completed at room temperature. The effects of four parameters including resin type, curing agent type, curing agent concentration and diluent quantity were investigated to design a resin formulation with a highest Tg after curing. The obtained results were quantitatively evaluated by the analysis of variance (ANOVA). The results of ANOVA showed that the highest Tg of 86.0 ± 9.0 °C was obtained for the optimum formulation of MANA POX-95 as epoxy resin, H-30 as curing agent and 52 phr H-30. The Tg measured by the experiment was 78.0 ± 0.9 °C. In addition, the single lap shear strength (adhesion strength) of the optimized insulator was measured at 13.66 ± 1.02 MPa. Pull-off test performed on the surface of DB propellant resulted a 1.935 ± 0.003 MPa adhesion strength.