Properties of Steel 12Kh18N10T Tested for Tensile Strength in Liquid Helium Cooled to 2.4 K

被引：0
|
作者：
G. A. Stepanov
V. V. Stanotina
机构：
[1] Kriogenmash Company,
来源：
Metal Science and Heat Treatment | 2003年 / 45卷
关键词：
Mechanical Property; Tensile Strength; Helium; Fracture Surface; Test Bench;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Mechanical properties of steel 12Kh18N10T (rolled sheets) and its welded joints are studied by testing smooth and notched specimens for tensile strength in liquid helium at 2.4 K using a test bench based on the UMÉ-10TM machine with a special low-temperature attachment. Fracture surfaces are studied and the properties of steel 12Kh18N10T are compared at 2.4 and 4.2 K.
引用
收藏
页码：373 / 375
页数：2
相关论文
共 50 条
  • [31] EFFECT OF REACTOR IRRADIATION ON THE HYDROGEN PERMEABILITY OF 12KH18N10T STEEL
    POLOSUKHIN, BG
    BASKAKOV, EP
    SULIMOV, EM
    GOLOVACHEV, MG
    ZYRYANOV, AP
    SOVIET ATOMIC ENERGY, 1990, 69 (05): : 993 - 994
  • [32] CONTACT THERMAL-DIFFUSION TITANIZATION OF STEEL 12KH18N10T
    PUTINA, OA
    NECHAEV, NP
    BONDAREVA, EP
    ZAITSEV, GA
    RAZZHIVINA, NV
    PROTECTION OF METALS, 1982, 18 (04): : 519 - 521
  • [33] Wear resistance of gasobaric nitrided layers on steel 12Kh18N10T
    S. A. Gerasimov
    M. A. Gress
    V. G. Lapteva
    G. G. Mukhin
    V. V. Bayazitova
    Metal Science and Heat Treatment, 2008, 50 : 73 - 76
  • [34] Effect of reactor irradiation on the hydrogen permeability of 12Kh18N10T steel
    Polosukhin, B.G.
    Baskakov, E.P.
    Sulimov, E.M.
    Golovachev, M.G.
    Zyryanov, A.P.
    Soviet atomic energy, 1991, 69 (05): : 993 - 994
  • [35] MORPHOLOGICAL PECULIARITIES OF THE DEVELOPMENT OF COVERED PITTINGS ON 12KH18N10T STEEL
    MESHCHERYAKOV, AV
    KISELEVA, LA
    KUZYUKOV, AN
    PROTECTION OF METALS, 1993, 29 (06): : 722 - 725
  • [36] HEAT-TREATMENT OF TIC 12KH18N10T CARBIDE STEEL
    GUREVICH, YG
    SAVINYKH, LM
    STEEL IN THE USSR, 1990, 20 (04): : 204 - 205
  • [37] Wear resistance of gasobaric nitrided layers on steel 12Kh18N10T
    Gerasimov, S. A.
    Gress, M. A.
    Lapteva, V. G.
    Mukhin, G. G.
    Bayazitova, V. V.
    METAL SCIENCE AND HEAT TREATMENT, 2008, 50 (1-2) : 73 - 76
  • [38] PHASE-COMPOSITION AND PROPERTIES OF DEFORMED STEEL 12KH18N10T AFTER PROLONGED HEATING
    SMIRNOV, MA
    TOLSTOV, AM
    BULANOV, YP
    KUZNETSOVA, GV
    VYPRYAZHKIN, VP
    METAL SCIENCE AND HEAT TREATMENT, 1979, 21 (1-2) : 34 - 38
  • [39] STRUCTURE AND PROPERTIES OF STEEL 12KH18N10T AFTER PROLONGED OPERATION AT-183DEGREESC
    STEPANOV, GA
    LOKHANKINA, LK
    GORBUNOV, VA
    METAL SCIENCE AND HEAT TREATMENT, 1976, 18 (5-6) : 430 - 432
  • [40] EFFECT OF WORKING TEMPERATURES ON THE PROPERTIES OF BRAZED JOINTS IN 12KH18N10T CORROSION RESISTING STEEL
    GRISHIN, VL
    WELDING PRODUCTION, 1982, 29 (07): : 32 - 33
12345