Corundum Ceramics for Medical Purposes

被引：0
|
作者：
E. S. Lukin
S. V. Tarasova
N. A. Popova
N. A. Makarov
机构：
[1] D. I. Mendeleev Russian Chemical Engineering University,
[2] ,undefined
来源：
Glass and Ceramics | 2003年 / 60卷
关键词：
Oxide; Polymer; Aluminum; Porosity; Heat Treatment;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The possibilities of using various kinds of aluminum oxide materials, modifying additives, and temporary technological binders for making bioinert ceramics based on aluminum oxide are considered. Regimes for heat treatment of intermediate pieces are developed. A ceramic material with a mean density of 4.01 g/cm3, three-point bending strength 380 ±20 MPa, a size of corundum crystal equal to 4 – 6 μm, and zero open porosity is obtained, which can be used in endoprostheses caps for coxofemoral joints.
引用
收藏
页码：26 / 29
页数：3
相关论文
共 50 条
  • [41] Production of High-Flexural-Strength Corundum Ceramics
    Panasyuk, G. P.
    Semenov, E. A.
    Kozerozhets, I. V.
    Danchevskaya, M. N.
    Lukin, E. S.
    Belan, V. N.
    Voroshilov, I. L.
    Azarova, L. A.
    Izotov, A. D.
    DOKLADY CHEMISTRY, 2019, 485 (2) : 116 - 118
  • [42] THE RESULTS AND PROSPECTS OF USING ENDOPROSTHESES MADE OF CORUNDUM CERAMICS
    GUDUSHAURI, ON
    DUMBADZE, GG
    MIKADZE, GS
    KHIRURGIYA, 1985, (11): : 124 - &
  • [43] Sintering specifics of corundum ceramics modified with eutectic additives
    N. A. Makarov
    Glass and Ceramics, 2006, 63 : 119 - 121
  • [44] Corundum ceramics with a eutectic zinc-bearing additive
    Makarov, NA
    Zhirnov, RV
    Popova, NA
    GLASS AND CERAMICS, 2002, 59 (7-8) : 232 - 233
  • [45] Production of High-Flexural-Strength Corundum Ceramics
    G. P. Panasyuk
    E. A. Semenov
    I. V. Kozerozhets
    M. N. Danchevskaya
    E. S. Lukin
    V. N. Belan
    I. L. Voroshilov
    L. A. Azarova
    A. D. Izotov
    Doklady Chemistry, 2019, 485 : 116 - 118
  • [46] Propagation of nonequilibrium phonons in corundum-based ceramics
    Ivanov, S. I.
    Taranov, A. V.
    Khazanov, E. N.
    Physics of the Solid State, 37 (10):
  • [47] Sintering specifics of corundum ceramics modified with eutectic additives
    Makarov, N. A.
    GLASS AND CERAMICS, 2006, 63 (3-4) : 119 - 121
  • [48] Deformation and Fracture of Corundum Ceramics with a Multilevel Pore Structure
    M. V. Grigor’ev
    A. G. Burlachenko
    S. P. Buyakova
    S. N. Kul’kov
    Technical Physics, 2019, 64 : 1803 - 1807
  • [49] Purposes in medical research
    Cohn, AE
    JOURNAL OF CLINICAL INVESTIGATION, 1924, 1 (01): : 1 - 11
  • [50] Use of corundum ceramics for fine milling of various materials
    Makarov, NA
    Lukin, ES
    Popova, NA
    Sidorin, VA
    GLASS AND CERAMICS, 2005, 62 (1-2) : 19 - 20
12345