Wettability characterization of transparent MgF2 nanoparticle coatings with SiO2 binder covered with fluoroalkylsilane self-assembled monolayers

SiO2-added MgF2 nanoparticle coatings with various surface roughness properties were formed on silica-glass substrates from autoclaved sols prepared at 100–180 °C. The samples were exposed to fluoro-alkyl silane (FAS) vapor to give hydrophobicity. All nanoparticle samples before FAS treatment had transmittances higher than 93% and such values were preserved even after FAS treatment. We examined root mean square roughnesses of the nanoparticle coatings with a Scanning Probe Microscope. We also examined their static and dynamic wettabilities with a contact angle meter and calculated their adhesive energies and surface free energies (SFEs). The surface roughness of the nanoparticle coating increased with the increase of the autoclave temperature. In addition, higher autoclave temperature caused increases in the sliding angle and decreases in the SFE. Interestingly, the higher the contact angle was, the larger the sliding angle was, although smaller sliding angle was expected with a larger contact angle.