Simple model of microsegregation during solidification of steels

被引：0
作者：
Young-Mok Won
Brian G. Thomas
机构：
[1] Pohang Iron & Steel Co. Ltd.,the Department of Mechanical and Industrial Engineering
[2] University of Illinois at Urbana-Champaign,undefined
来源：
Metallurgical and Materials Transactions A | 2001年 / 32卷
关键词：
Cool Rate; Material Transaction; Solid Fraction; Solidus Temperature; Iron Steel Inst;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A simple analytical model of microsegregation for the solidification of multicomponent steel alloys is presented. This model is based on the Clyne-Kurz model and is extended to take into account the effects of multiple components, a columnar dendrite microstructure, coarsening, and the δ/γ transformation. A new empirical equation to predict secondary dendrite arm spacing as a function of cooling rate and carbon content is presented, based on experimental data measured by several different researchers. The simple microsegregation model is applied to predict phase fractions during solidification, microsegregation of solute elements, and the solidus temperature. The predictions agree well with a range of measured data and the results of a complete finite-difference model. The solidus temperature decreases with either increasing cooling rate or increasing secondary dendrite arm spacing. However, the secondary dendrite arm spacing during solidification decreases with increasing cooling rate. These two opposite effects partly cancel each other, so the solidus temperature does not change much during solidification of a real casting.
引用
收藏
页码：1755 / 1767
页数：12
相关论文
共 113 条
  • [11] Kitagawa T.(1999)undefined J. Cryst. Growth 199 1275-80
  • [12] Kawakami K.(1999)undefined Iron Steel Inst. Jpn. Int. 39 730-36
  • [13] El-Bealy M.(2000)undefined Physica D 138 114-33
  • [14] Voller V.R.(2000)undefined Math. Methods Appl. Sci. 23 491-513
  • [15] Beckermann C.(1984)undefined Trans. Iron Steel Inst. Jpn. 24 873-82
  • [16] Miettinen J.(1986)undefined Metall. Trans. B 17B 845-59
  • [17] Wang C.Y.(1996)undefined Iron Steel Inst. Jpn. Int. 36 284-89
  • [18] Beckermann C.(1998)undefined Iron Steel Inst. Jpn. Int. 38 1093-99
  • [19] McCarthy J.F.(1984)undefined Metall. Trans. A 17A 2063-73
  • [20] Karma A.(1992)undefined Tetsu-to-Hagané 78 587-93
12345678910