Special features of the formation of microstructure of heat-treated low-alloy steel

被引：0

作者：

V. I. Spivakov

I. G. Uzlov

L. A. Moiseeva

É. A. Orlov

L. S. Tikhonyuk

机构：

[1] Institute of Ferrous Metallurgy of the National Academy of Sciences of Ukraine,Azovstal' Iron and Steel Integrated Works

来源：

Metal Science and Heat Treatment | 1998年 / 40卷

关键词：

Ferrite; Austenite; Bainite; Pearlite; Accelerate Cool;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The strength and the operational properties of low-alloy thick-sheet steels is increased by heat treatment in the line of the mill with the use of the rolling or furnace heat. The present work concerns the special features of structure formation and the mechanical properties of rolled stock from sheet structural steel 09G2S with a strength level C345 (σy=325-345 MPa) in a hot-rolled and a normalized state after accelerated cooling from the normalizing furnace and after rolling behind the finishing stand. As a result of the rapid cooling in the line of the mill the sheet acquires properties corresponding to steels with a C390–C440 strength level (σy=390-440 MPa).

引用

页码：313 / 315

页数：2