Radio-photoluminescence phenomenon in Ag-doped Cs2O–MgO–Al2O3–P2O5 glasses

被引：0
作者：
Akihiro Nishikawa
Daiki Shiratori
Prom Kantuptim
Takumi Kato
Daisuke Nakauchi
Noriaki Kawaguchi
Takayuki Yanagida
机构：
[1] Nara Institute of Science and Technology,
来源：
Journal of Materials Science: Materials in Electronics | 2023年 / 34卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, we successfully made Ag2O–Cs2O–MgO–Al2O3–P2O5 glasses with different Ag concentrations (0, 0.1, 0.3, 1.0, and 3.0 mol.%) by the melt-quenching method. We measured photoluminescence (PL) properties, the radio-photoluminescence (RPL) phenomenon, and spatial resolution on the X-ray imaging to check the capability of RPL imaging plate. RPL was observed in the Ag-doped samples by irradiating X-rays, and the new emission appeared at around 620 nm. According to the shape of the PL spectrum and lifetime, the emission was confirmed to be due to Ag2+ with lifetimes of 14.0–15.9 ns. In the X-ray imaging resolution test, the 3.0% Ag-doped sample had a spatial resolution of at least 10.0 LP/mm.
引用
收藏
相关论文
共 50 条
[21]   Characterization of Ag2O:MoO3:P2O5 glasses [J].
Chowdari, B.V.R. ;
Gopalakrishnan, R. ;
Tang, S.H. ;
Kuok, M.H. .
Solid State Ionics, 1988, 28-30 :704-709
[22]   Selective Crystallization Behavior of CaO-SiO2-Al2O3-MgO-FetO-P2O5 Steelmaking Slags Modified through P2O5 and Al2O3 [J].
Wang, Zhanjun ;
Sun, Yongqi ;
Sridhar, Seetharaman ;
Zhang, Mei ;
Guo, Min ;
Zhang, Zuotai .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2015, 46 (05) :2246-2254
[23]   Selective Crystallization Behavior of CaO-SiO2-Al2O3-MgO-FetO-P2O5 Steelmaking Slags Modified through P2O5 and Al2O3 [J].
Zhanjun Wang ;
Yongqi Sun ;
Seetharaman Sridhar ;
Mei Zhang ;
Min Guo ;
Zuotai Zhang .
Metallurgical and Materials Transactions B, 2015, 46 :2246-2254
[24]   Kinetics of mechanically activated P2O5 incorporation into Al2O3 [J].
N. F. Kosenko ;
M. A. Smirnova ;
O. P. Denisova .
Inorganic Materials, 2005, 41 :261-263
[25]   Kinetics of mechanically activated P2O5 incorporation into Al2O3 [J].
Kosenko, NF ;
Smirnova, MA ;
Denisova, OP .
INORGANIC MATERIALS, 2005, 41 (03) :261-263
[26]   Preparation and Characterization of Transparent Semiconducting Silica Nanocomposites Doped with P2O5 and Al2O3 [J].
El Nahrawy, Amany M. ;
Abou Hammad, Ali B. ;
Mansour, A. M. .
SILICON, 2021, 13 (10) :3733-3739
[27]   Preparation and Characterization of Transparent Semiconducting Silica Nanocomposites Doped with P2O5 and Al2O3 [J].
Amany M. El Nahrawy ;
Ali B. Abou Hammad ;
A. M. Mansour .
Silicon, 2021, 13 :3733-3739
[28]   Optical and photoluminescence characteristics of Pr3+-doped P2O5 +BaO+La2O3 glasses [J].
Kesavulu, C. R. ;
Basavapoornima, Ch. ;
Ramprasad, Pikkili ;
Deviprasad, C. J. ;
Depuru, Shobha Rani ;
Jayasankar, C. K. .
CHEMICAL PHYSICS IMPACT, 2025, 10
[29]   Dy3+-doped P2O5–Al2O3–K2O–CaF2–LiF glasses: thermal, spectroluminescence and photometric properties [J].
K Kiran Kumar ;
Ramachari Doddoji ;
V B Sreedhar ;
Nguyen Thi Quynh Lien ;
Ho Van Tuyen ;
Vasudeva Reddy Minnam Reddy .
Bulletin of Materials Science, 2022, 45
[30]   Effect of Al2O3 on structure and properties of Al2O3-K2O-P2O5 glasses [J].
Yue, Yu ;
Wang, Yajie ;
Cao, Yabin ;
Chen, Si ;
Zhou, Qinling ;
Chen, Wei ;
Hu, Lili .
OPTICAL MATERIALS EXPRESS, 2018, 8 (02) :245-258
12345