Sintering of ultra-fine tetragonal yttria-stabilized zirconia ceramics

被引：0

作者：

Hwan-Cheol Kim

In-Jin Shon

In-Kyoon Jeong

In-Yong Ko

Z. A. Munir

机构：

[1] Chonbuk National University,Department of Advanced Materials Engineering, Research Center of Advanced Materials Development, Engineering Research Institute

[2] University of California,Facility for Advanced Combustion Synthesis, Department of Chemical Engineering and Materials Science

来源：

Journal of Materials Science | 2007年 / 42卷

关键词：

Zirconia; Fracture Toughness; Sinter Temperature; Spark Plasma Sinter; Solid Oxide Fuel Cell;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

High-frequency induction heated sintering (HFIHS) is utilized to consolidate ultra-fine grain tetragonal zirconia stabilized with 3 mol%Y2O3 (3Y-SZ) ceramics. Densification to near theoretical density in a relatively short time can be accomplished using this method. Samples of 3Y-SZ with a relative density of up to 99.5% and an average grain size of about 170 nm could be obtained by sintering at 950 °C for 5 min under a pressure of 100 MPa pressure. The influence of sintering temperature and mechanical pressure on the final density and grain size of the sintered products was investigated. The sintered materials had fracture toughness and hardness values of 4.4 MPa m1/2 and 10.7 GPa, respectively.

引用

页码：9409 / 9414

页数：5

共 50 条

[41] Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing [J].

Koyama, Taku ;

Sato, Toru ;

Yoshinari, Masao .

DENTAL MATERIALS JOURNAL, 2012, 31 (06) :1103-1110

[42] Charge kinetics in spinel and yttria-stabilized zirconia [J].

Boughariou, Aicha ;

Karray, Fekri ;

Kallel, Ali ;

Blaise, Guy .

APPLIED SURFACE SCIENCE, 2009, 255 (09) :4779-4781

[43] Grain boundary energies in yttria-stabilized zirconia [J].

Dillon, Shen J. ;

Shen, Yu-Feng ;

Rohrer, Gregory S. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2022, 105 (04) :2925-2931

[44] Biomimetic apatite coating on yttria-stabilized tetragonal zirconia utilizing femtosecond laser surface processing [J].

Oyane, Ayako ;

Kakehata, Masayuki ;

Sakamaki, Ikuko ;

Pyatenko, Alexander ;

Yashiro, Hidehiko ;

Ito, Atsuo ;

Torizuka, Kenji .

SURFACE & COATINGS TECHNOLOGY, 2016, 296 :88-95

[45] Rapid 24 GHz microwave sintering of alumina - yttria-stabilized zirconia ceramic composites [J].

Egorov, S. V. ;

Eremeev, A. G. ;

Kholoptsev, V. V. ;

Plotnikov, I. V. ;

Rybakov, K. I. ;

Sorokin, A. A. ;

Balabanov, S. S. ;

Rostokina, E. Ye. .

CERAMICS INTERNATIONAL, 2024, 50 (22) :45155-45164

[46] The Effect of Sintering Temperature on the Phase Composition, Microstructure, and Mechanical Properties of Yttria-Stabilized Zirconia [J].

Kulyk, Volodymyr ;

Duriagina, Zoia ;

Vasyliv, Bogdan ;

Vavrukh, Valentyna ;

Kovbasiuk, Taras ;

Lyutyy, Pavlo ;

Vira, Volodymyr .

MATERIALS, 2022, 15 (08)

[47] Spark-plasma sintering the 8-mol% yttria-stabilized zirconia electrolyte [J].

Yang Bangchao ;

Jian Jiawen ;

Zhang Yican .

Journal of Materials Science, 2004, 39 :6863-6865

[48] Flash sintering of a three-phase alumina, spinel, and yttria-stabilized zirconia composite [J].

Kok, David ;

Jha, Shikhar Krishn ;

Raj, Rishi ;

Mecartney, Martha L. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2017, 100 (07) :3262-3268

[49] Heat capacity and thermodynamic functions of zirconia and yttria-stabilized zirconia [J].

Tojo, T ;

Atake, T ;

Mori, T ;

Yamamura, H .

JOURNAL OF CHEMICAL THERMODYNAMICS, 1999, 31 (07) :831-845

[50] Synthesis and thermal stability of zirconia and yttria-stabilized zirconia microspheres [J].

Leib, Elisabeth W. ;

Vainio, Ulla ;

Pasquarelli, Robert M. ;

Kus, Jonas ;

Czaschke, Christian ;

Walter, Nils ;

Janssen, Rolf ;

Mueller, Martin ;

Schreyer, Andreas ;

Weller, Horst ;

Vossmeyer, Tobias .

JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2015, 448 :582-592

← 1 2 3 4 5 →