Biosynthesis and Characterization of Poly-(3-hydroxybutyrate-co-3-hydroxyvalerate) from Bacillus cereus S10

The biodegradable and biocompatible copolymer poly-(3-hydroxybutyrate-co-5 mol% 3-hydroxyvalerate), poly-(3HB-co-5 mol% 3HV), was synthesized by Bacillus cereus S10 and the highest yield was determined as 69.91 % at pH 7 and 30 °C after 48 h of incubation using a glucose as the sole carbon source. Poly-(3HB-co-5 mol% 3HV) was purified from bacterial biomass using chloroform. FTIR analysis showed absorption bands at 1,723, 1,274, 1,373, 1,453, 2,932 cm−1 corresponding to C=O, C–O stretching, CH3, –CH2 and –CH groups, respectively. 1H-NMR and 13C-NMR analysis confirmed that the copolymer was composed of 95 mol% of 3-hydroxybutrate and 5 mol% of 3-HV monomeric units. Poly-(3-HB-co-5 mol% 3HV) was used for nanoparticles preparation. The diameter of nanoparticles was 202 nm.