Corrosion resistance of float glass

被引：0
|
作者：
N. V. Temnyakova
L. A. Shitova
E. V. Yuneva
E. P. Zinina
机构：
[1] Saratov Glass Institute JSC,
来源：
Glass and Ceramics | 2009年 / 66卷
关键词：
Corrosion Resistance; Glass Surface; Glass Sample; Glass Sheet; Domestic Industry;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion resistance of float glass has been investigated in the course of climatic tests. It is shown that the main surface defects of tempered glass are leaching and “burnt-on paper and sulfurous film.” The properties of various interleaving materials used in the domestic industry are studied. The corrosion resistance of tempered glass depends on the surface of the initial glass and the properties of the interleaving material used for packing the initial as well as the tempered glass.
引用
收藏
页码：79 / 81
页数：2
相关论文
共 50 条
  • [41] Raman spectroscopy study of glass corrosion
    Hruska, Branislav
    Gavenda, Tadeas
    Vasicek, Filip
    Svoboda, Roman
    VIBRATIONAL SPECTROSCOPY, 2020, 109
  • [42] Effect of Acid Treatment on Surface Morphology and Strength of Float Glass under Ultrasonic Wave
    Diao, Yunchao
    Jiang, Yanyan
    Wang, Shikai
    Wang, Chengyu
    MANUFACTURING SCIENCE AND TECHNOLOGY, PTS 1-3, 2011, 295-297 : 1660 - +
  • [43] Effect of Cr Element on Glass Forming Ability and Corrosion Resistance of Fe-based Bulk Amorphous Alloys
    Xiong Bin
    Li Xue
    Zheng Jibo
    Li Xining
    Lu Gonghao
    Wang Zhenmin
    Ju Dongying
    Akihiro, Makino
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (02) : 701 - 704
  • [44] Effect of W on the thermal stability, mechanical properties and corrosion resistance of Fe-based bulk metallic glass
    Zhang, Xuanpeng
    Lai, Limin
    Xiao, Siming
    Zhang, Hongju
    Zhang, Feifei
    Li, Ning
    Guo, Shengfeng
    INTERMETALLICS, 2022, 143
  • [45] Effects of additional element on the glass forming ability and corrosion resistance of bulk Zr-based amorphous alloys
    Zhang Hui
    Zhang Guo-Ying
    Yang Shuang
    Wu Di
    Qi Ke-Zhen
    ACTA PHYSICA SINICA, 2008, 57 (12) : 7822 - 7826
  • [46] Effects of Si Additions on the Glass-Forming Ability and Corrosion Resistance of Cu49Zr45Al6 Bulk Metallic Glass
    Su, E. L.
    Wu, X. Q.
    Zhang, D. C.
    Li, Y.
    Lin, J. G.
    CORROSION, 2013, 69 (11) : 1088 - 1094
  • [47] Effects of glass transition temperatures of films on the corrosion resistance after forming of pre-coated aluminum sheets
    Hattori, Nobuo
    Tanigawa, Masaki
    Okido, Masazurni
    MATERIALS TRANSACTIONS, 2008, 49 (05) : 1180 - 1185
  • [48] Controlling the static quenching temperature to improve the corrosion resistance performance of Zr-based bulk metallic glass
    Guo, Chuan
    Liu, Guanting
    Zhang, Shuyan
    Wang, Tuo
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2025, 660
  • [49] Effects of Cr contents in Fe-based bulk metallic glasses on the glass forming ability and the corrosion resistance
    Wang, S. L.
    Li, H. X.
    Zhang, X. F.
    Yi, S.
    MATERIALS CHEMISTRY AND PHYSICS, 2009, 113 (2-3) : 878 - 883
  • [50] Tubing with high corrosion resistance
    A. V. Ioffe
    T. V. Tetyueva
    M. A. Vyboyshchik
    E. A. Trifonova
    E. S. Lutsenko
    Metal Science and Heat Treatment, 2010, 52 : 13 - 19
12345