Simultaneous synthesis and consolidation of nanostuctured MgAl2O4 compound by high-frequency induction heated sintering

被引：0
作者：
In-Jin Shon
Seung-Mi Kwak
Jung-Mann Doh
Bang-Ju Park
Jin-Kook Yoon
机构：
[1] Chonbuk National University,Division of Advanced Materials Engineering and the Research Center of Advanced Materials Development, Engineering College
[2] Korea Institute of Science and Technology,Advanced Functional Materials Research Center
[3] Gachon University,College of BioNano Tech
来源：
Research on Chemical Intermediates | 2013年 / 39卷
关键词：
Sintering; MgAl; O; Nanostructured material; Powder metallurgy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The rapid sintering of a nanostuctured MgAl2O4 compound in a short time was investigated with high-frequency induction heating sintering process. The advantage of this process is that it allows very quick densification to near theoretical density and prohibition of grain growth in nanostuctured materials. A highly dense nanostructured MgAl2O4 compound was produced with simultaneous application of 80 MPa pressure and induced current with output of total power capacity (15 kW) within 2 min. The sintering behavior, grain size, and mechanical properties of the MgAl2O4 compound were investigated.
引用
收藏
页码：1291 / 1299
页数：8
相关论文
共 67 条
  • [1] Anappan S(2004)undefined Mater. Lett. 58 2283-2289
  • [2] Berchmans LJ(1995)undefined J. Am. Ceram. Soc. 78 1857-1862
  • [3] Augustin CO(1976)undefined J. Mater. Sci. 11 1919-1926
  • [4] Baudin C(2000)undefined J. Alloys Compd. 305 225-238
  • [5] Martinez R(2001)undefined Scr. Mater. 44 1061-1068
  • [6] Pena P(1997)undefined Prog. Mater. 42 311-320
  • [7] Hing P(1995)undefined Int. J. Refract. Met. Hard Mater. 13 297-303
  • [8] Sherif El-Eskandarany M(2011)undefined Met. Mater. Int. 17 57-61
  • [9] Fu L(2011)undefined Electron. Mater. Lett. 70 133-137
  • [10] Cao LH(2007)undefined Scr. Mater. 56 561-564
1234567