Surface Severe Plastically Deformed Nanostructured AA7075 Alloy: Assessment on Tribological and Axial Fatigue Behaviors

被引：0
作者：
Yusuf Efe
Ibrahim Karademir
Fazil Husem
Erfan Maleki
Okan Unal
机构：
[1] Karabuk University,Mechanical Engineering Department
[2] Bartın University,Mechanical Engineering Department
[3] Karabuk University,Modern Surface Engineering Laboratory (MSELAB)
[4] Karabuk University,TOBB Technical Sciences Vocational School
[5] Sharif University of Technology-International Campus,Mechanical Engineering Department
[6] Politecnico di Milano,Department of Mechanical Engineering
来源：
Journal of Materials Engineering and Performance | 2020年 / 29卷
关键词：
axial fatigue; grain refinement; residual stress; severe shot peening;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
AA7075 alloy is exposed to severe shot peening (SSP) with an Almen intensity of 20A. The microstructure is analyzed via FEGSEM and EBSD microscopy. X-ray diffraction (XRD) analysis is used to evaluate the crystallite size in terms of FWHM measurements. The residual stress measurements show a thicker compressed layer (600 µm) formed by SSP. Microhardness improvements are observed as 30% on topmost surface and releases substantially after 600 µm. Coefficient of friction (COF) of treated material remains higher throughout the sliding distance, however, is reduced particularly in the early stage of sliding distance for the wear load of 20 N. The effect of SSP is vanished particularly at lower loads with longer sliding distances. Besides, improvement on fatigue behavior is observed after SSP despite the increase of roughness remarkably.
引用
收藏
页码：3774 / 3783
页数：9
相关论文
共 204 条
  • [1] Pandey V(2016)Low Cycle Fatigue Behavior of AA7075 with Surface Gradient Structure Produced by Ultrasonic Shot Peening Procedia Struct. Integrity 2 3288-3295
  • [2] Chattopadhyay K(2010)The Effects of Multiple Re-shot Peening on Fretting Fatigue Behavior of Al7075-T6 Surf. Coat. Technol. 205 102-109
  • [3] Srinivas NCS(2009)Fatigue Properties and Crack Behavior of Ultra-Fine and Nanocrystalline Pure Metals Int. J. Fatigue 31 1476-1489
  • [4] Singh V(2012)Thermal Stability of Nanocrystallized Surface Produced by Surface Mechanical Attrition Treatment in Aluminum Alloys Surf. Coat. Technol. 206 3970-3980
  • [5] Majzoobi GH(2018)Wear Behavior of Mg-3Al-1Zn Alloy Subjected to Laser Shock Peening Surf. Coat. Technol. 337 501-509
  • [6] Ahmadkhani AR(2016)Combining Thermo-Diffusing Titanium and Plasma Nitriding to Modify C61900 Cu–Al Alloy Vacuum 126 41-44
  • [7] Cavaliere P(2018)Effect of Severe Shot Peening and Ultra-Low Temperature Plasma Nitriding on Ti-6Al-4V Alloy Vacuum 150 69-78
  • [8] Chang HW(2013)Fatigue Behavior of X70 Microalloyed Steel After Severe Shot Peening Int. J. Fatigue 55 33-42
  • [9] Kelly PM(2020)Fatigue Properties of Nanocrystallized Surfaces Obtained by High Energy Shot Peening Procedia Eng. 2 1683-1690
  • [10] Shi YN(2013)Fatigue Behavior of Notched Steel Specimens with Nanocrystallized Surface Obtained by Severe Shot Peening Mater. Des. 45 497-503
12345678910