Fatigue crack propagation under variable amplitude loading in PMMA and bone cement

被引：0
|
作者：
S. L. Evans
机构：
[1] Cardiff University,School of Engineering
来源：
Journal of Materials Science: Materials in Medicine | 2007年 / 18卷
关键词：
PMMA; Crack Growth Rate; Fatigue Crack Growth; Bone Cement; Crack Path;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Fatigue failure of PMMA bone cement is an important factor in the failure of cemented joint replacements. Although these devices experience widely varying loads within the body, there has been little or no study of the effects of variable amplitude loading (VAL) on fatigue damage development.
引用
收藏
页码：1711 / 1717
页数：6
相关论文
共 50 条
  • [21] Fatigue and creep-fatigue crack growth in aviation turbine disk simulation models under variable amplitude loading
    Shlyannikov, V
    Sulamanidze, A.
    Yarullin, R.
    ENGINEERING FAILURE ANALYSIS, 2022, 131
  • [22] Fatigue crack growth of Al 7475 T761 under constant and variable amplitude loading
    Pereira, CPM
    Voorwald, HJC
    ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, : 1483 - 1490
  • [23] Effect of plasma nitriding on fatigue crack growth on AISI 4140 steel under variable amplitude loading
    Sengul, A. B.
    Celik, A.
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 (21-22) : 5172 - 5177
  • [24] Delamination in Fiber Metal Laminates (GLARE) during fatigue crack growth under variable amplitude loading
    Khan, S. U.
    Alderliesten, R. C.
    Benedictus, R.
    INTERNATIONAL JOURNAL OF FATIGUE, 2011, 33 (09) : 1292 - 1303
  • [25] Experimental fatigue crack growth behavior and predictions under multiaxial variable amplitude service loading histories
    Gates, Nicholas R.
    Fatemi, Ali
    ENGINEERING FRACTURE MECHANICS, 2017, 174 : 80 - 103
  • [26] Closure effects on fatigue crack growth rates at constant and variable amplitude loading
    Månsson, T
    Öberg, H
    Nilsson, F
    ENGINEERING FRACTURE MECHANICS, 2004, 71 (9-10) : 1273 - 1288
  • [27] Fatigue crack closure evaluation under constant amplitude and spectrum loading
    Parida, BK
    Manjunatha, CM
    Girish, HM
    JOURNAL OF TESTING AND EVALUATION, 2003, 31 (04) : 337 - 346
  • [28] Constraint corrected cycle-by-cycle analysis of crack growth retardation under variable amplitude fatigue loading
    Zhang, Jie
    Muys, Louis
    De Tender, Steven
    Micone, Nahuel
    Hertele, Stijn
    De Waele, Wim
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 125 : 199 - 209
  • [29] Reliability analysis of fatigue crack growth for rail steel under variable amplitude service loading conditions and wear
    Nejad, Reza Masoudi
    Liu, Zhiliang
    Ma, Wenchen
    Berto, Filippo
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 152
  • [30] Corrosion fatigue crack growth behavior of pipeline steel under underload-type variable amplitude loading schemes
    Yu, Mengshan
    Xing, Xiao
    Zhang, Hao
    Zhao, Jiaxi
    Eadie, Reg
    Chen, Weixing
    Been, Jenny
    Van Boven, Greg
    Kania, Richard
    ACTA MATERIALIA, 2015, 96 : 159 - 169
12345