X-ray Diffraction Study of the Nanostructure Resulting from Decomposition of (ZrC)1 –x(NbC)x Solid Solutions

被引：0
作者：
A. I. Gusev
S. V. Rempel'
机构：
[1] Institute of Solid-State Chemistry,Ural Division, Russian Academy of Sciences
来源：
Inorganic Materials | 2003年 / 39卷
关键词：
Inorganic Chemistry; Solid Solution; Diffraction Study; Peak Width; Diffraction Angle;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Solid-state decomposition of nearly equimolar ZrC–NbC solid solutions was studied by x-ray diffraction. The results demonstrate that annealing broadens the diffraction peaks from the solid solutions. Analysis of the peak width as a function of the diffraction angle indicates that the broadening is due to the decomposition of the solid solution into two coherent isostructural (B1) phases close in lattice parameter (0.4573 and 0.4561 nm) and the formation of nanometer-sized (≃70 nm) grains. The nanostructure remains stable during long-term (100 to 700 h) annealing between 670 and 1270 K.
引用
收藏
页码：43 / 47
页数：4
相关论文
共 50 条
[21]   Rietveld refinement of tetragonal V4+-ZrO2 solid solutions obtained from gels by X-ray powder diffraction [J].
Torres, FJ ;
Amigó, JM ;
Alarcón, J .
JOURNAL OF SOLID STATE CHEMISTRY, 2002, 163 (01) :33-36
[22]   Formation of Ir–MgO Solid Solutions Analyzed with X-ray Absorption Spectroscopy [J].
Kazu Okumura ;
Hitomi Hoshi ;
Hikaru Iiyoshi .
Catalysis Surveys from Asia, 2023, 27 :95-106
[23]   Numerical separation of background in X-ray diffraction studies [J].
S. A. Suevalov ;
I. G. Kaplan .
Crystallography Reports, 2005, 50 :31-35
[24]   Numerical separation of background in X-ray diffraction studies [J].
Suevalov, SA ;
Kaplan, IG .
CRYSTALLOGRAPHY REPORTS, 2005, 50 (01) :31-35
[25]   X-ray Diffraction Study of an Inhomogeneous Langasite (La3Ga5SiO14) Crystal [J].
G. M. Kuz'micheva ;
V. B. Rybakov ;
E. N. Domoroshchina ;
A. B. Dubovskii .
Inorganic Materials, 2002, 38 :1040-1047
[26]   X-ray diffraction study of an inhomogeneous langasite (La3Ga5SiO14) crystal [J].
Kuz'micheva, GM ;
Rybakov, VB ;
Domoroshchina, EN ;
Dubovskii, AB .
INORGANIC MATERIALS, 2002, 38 (10) :1040-1047
[27]   X-ray diffraction determination of the degree of ordering of a solid solution in epitaxial AlGaN layers [J].
R. N. Kyutt ;
S. V. Ivanov .
Physics of the Solid State, 2014, 56 :2390-2392
[28]   X-ray photoelectron spectroscopy study of the electronic structure of La1–xCaxMnO3+δ solid solutions [J].
S. H. Estemirova ;
A. V. Fetisov ;
V. B. Fetisov .
Journal of Applied Spectroscopy, 2009, 76 :394-401
[29]   Hard X-ray diffraction studies of La1-xSrxMnO3 [J].
Niemöller, T ;
von Zimmermann, M ;
Schneider, JR ;
Frello, T ;
Andersen, NH ;
Uhlenbruck, S ;
Friedt, O ;
Büchner, B ;
Berthet, P ;
Pinsard, L ;
Revcolevschi, A .
JOURNAL OF SUPERCONDUCTIVITY, 1999, 12 (01) :317-318
[30]   X-ray diffraction study of the complex of the enzyme SAICAR synthase with substrate analogues [J].
D. V. Urusova ;
S. V. Antonyuk ;
A. I. Grebenko ;
V. S. Lamzin ;
V. R. Melik-Adamyan .
Crystallography Reports, 2003, 48 :763-767
12345