Increasing Solidification Rate of M2 High-Speed Steel Ingot by Fusible Metal Mold

被引：0
作者：
Yan-Liang Ji
Wei Zhang
Xiao-Yang Chen
Jian-Guo Li
机构：
[1] Shanghai Jiao Tong University,School of Materials Science and Engineering
来源：
Acta Metallurgica Sinica (English Letters) | 2016年 / 29卷
关键词：
Carbide; Cooling rate; Solidification process; Microstructure; Dendritic spacing;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
As one of the most popular used high-speed steels, M2 possesses excellent hardness and toughness as cutting tools. Networks of eutectic carbides distributing in the inter-dendritic region are academically considered to be the typical microstructure of M2, which can be refined by increasing cooling rate. In this paper, a novel casting method named fusible metal mold (FMM) is employed to refine the microstructure of M2 high-speed steel. Results show that FMM casting method can improve cooling rate by 100% without any contamination of the melts’ composition.
引用
收藏
页码：382 / 387
页数：5
相关论文
共 78 条
  • [1] Boccalini M(2011)undefined Int. Mater. Rev. 46 92-undefined
  • [2] Goldenstein H(2014)undefined Mater. Sci. Technol. Lond. 30 116-undefined
  • [3] Zhou XF(2014)undefined J. Iron. Steel Res. Int. 21 60-undefined
  • [4] Fang F(2011)undefined China Foundry 8 290-undefined
  • [5] Jiang JQ(2006)undefined Iron Steel 41 63-undefined
  • [6] Zhu WL(1986)undefined T. Iron Steel I. Jpn. 26 305-undefined
  • [7] Xu HX(2000)undefined ISIJ Int. 40 980-undefined
  • [8] Qu MG(2014)undefined Key Eng. Mater. 592–693 680-undefined
  • [9] Sun SH(2013)undefined Weld. Int. 27 1-undefined
  • [10] Bai XH(2003)undefined Acta Metall. Sin. (Engl. Lett.) 16 524-undefined
12345678