Surface modification of PVDF porous membranes

A novel method for the surface modification of PVDF porous membranes was introduced. Styrene-(N-(4-hydroxyphenyl) maleimide) alternating copolymer SHMI-Br was blended with PVDF to fabricate SHMI-Br/PVDF membranes. The C-Br bond on the SHMI-Br/PVDF membrane was served as initial site of ATRP, and P(PEGMA) brush was grafted on the PVDF membrane. Attenuated total reflectance-Fourier transform infrared spectroscopy (ATR/FTIR) was used to prove the P(PEGMA) brushes were successfully grafted onto the SHMI-Br/PVDF membrane surface. Introduction of P(PEGMA) brushes on the PVDF membrane surface enhanced the hydrophilicity effectively. When the PEGMA degree of grafting was 16.7 wt%, the initial contact angle of PVDF membrane decreased from 98° to 42°. The anti-fouling ability of PVDF membrane was improved significantly after P(PEGMA) brush was grafted. Taking the PEGMA degree of grafting 16.7 wt% as an example, the flux of protein solution was about 151.21 L/(m2 h) when the pH value of the BSA solution was 4.9. As the pH value was increased to 7.4, the flux was changed to 180.06 L/(m2 h). However, the protein solution flux of membrane M3 (PEGMA: 0 wt%) was only 73.84 L/(m2 h) and 113.52 L/(m2 h) at pH 4.9 and 7.4, respectively.