Hybrid transparent electrodes of silver nanowires and carbon nanotubes: a low-temperature solution process

被引：0
作者：
Takehiro Tokuno
Masaya Nogi
Jinting Jiu
Katsuaki Suganuma
机构：
[1] Osaka University,The Institute of Scientific and Industrial Research (ISIR)
来源：
Nanoscale Research Letters | / 7卷
关键词：
Silver nanowire; Carbon nanotube; Low-temperature process; Solution process;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Hybrid transparent electrodes with silver nanowires (AgNWs) and single-walled carbon nanotubes (SWCNTs) were fabricated on plastic films by a low-temperature solution process. The hybrid transparent electrodes exhibited a sheet resistance of 29.2 Ω/sq with a transparency of 80% when 6 wt.% of SWCNTs was mixed with AgNWs. This sheet resistance was less than one-fourth that of the AgNW transparent electrodes that were prepared using the same method. This reduction in sheet resistance is because the SWCNTs formed bridges between the AgNWs, thus, resulting in high conductivity of the hybrid transparent electrodes. The hybrid electrodes formed on plastic films exhibited high conductivity as well as excellent stability in sheet resistance when tested using a repeated bending test.
引用
收藏
相关论文
共 184 条
[1]  
Kumar A(2010)The race to replace tin-doped indium oxide: which material will win? ACS Nano 4 11-14
[2]  
Zhou C(2011)Emerging transparent electrodes based on thin films of carbon nanotubes, graphene, and metallic nanostructures Adv Mater 23 1482-1513
[3]  
Hecht DS(2004)Transparent, conductive, carbon nanotube films Science 305 1273-1276
[4]  
Hu L(2004)Percolation in transparent and conducting carbon nanotube networks Nano Lett 4 2513-2517
[5]  
Irvin G(2005)Strong, transparent, multifunctional, carbon nanotube sheets Science 309 1215-1219
[6]  
Wu Z(2006)Carbon nanotube films for transparent and plastic electronics J Mater Chem 16 3533-3539
[7]  
Chen Z(2006)A method of printing carbon nanotube thin films Appl Phys Lett 88 123109-1274
[8]  
Du X(2008)Transparent conductive single-walled carbon nanotube networks with precisely tunable ratios of semiconducting and metallic nanotubes ACS Nano 2 1266-3216
[9]  
Logan JM(2009)Ultrasmooth, large-area, high-uniformity, conductive transparent single-walled carbon-nanotube films for photovoltaics produced by ultrasonic spraying Adv Mater 21 3210-2473
[10]  
Sippel J(2009)The spatial uniformity and electromechanical stability of transparent, conductive films of single walled nanotubes Carbon 47 2466-274
12345678910