Slurry Erosion Behavior of HVOF-Sprayed Amorphous Coating on Stainless Steel

被引：0
作者：
S. Vignesh
V. Balasubramanian
K. Sridhar
D. Thirumalaikumarasamy
机构：
[1] Annamalai University,Centre for Materials Joining and Research (CEMAJOR), Department of Manufacturing Engineering
[2] Naval Materials Research Laboratory (NMRL),Department of Mechanical Engineering
[3] Government College of Engineering,undefined
[4] Bargur,undefined
来源：
Metallography, Microstructure, and Analysis | 2019年 / 8卷
关键词：
High-velocity oxy-fuel spraying; Amorphous coating; Microstructure; Slurry erosion;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The slurry erosion behavior of high-velocity oxy-fuel-sprayed iron-based amorphous coatings and the reference stainless steel were both investigated. The slurry erosion–corrosion test was performed in a rotating disk rig facility with circulating system using distilled water and 3.5 wt.% NaCl slurries. The performance of uncoated substrate and as-coated samples was evaluated at various operating parameters, namely impingement angle, slurry concentration, and specimen rotational speed. The effects of the slurry erosion parameters on the microstructure and the properties of the coatings were systematically studied. The wear mechanisms of coated and uncoated samples were investigated using scanning electron microscopy. The results showed that amorphous coating exhibited higher slurry erosion–corrosion resistance compared to the stainless steel.
引用
收藏
页码：462 / 471
页数：9
相关论文
共 108 条
[1]  
Wood RJK(2004)Erosion–corrosion of candidate HVOF aluminium-based marine coatings Wear 256 545-556
[2]  
Speyer AJ(2007)Slurry erosion of thermal spray coatings and stainless steels for hydraulic machinery Wear 263 258-264
[3]  
Santa JF(2014)To study the slurry erosion behaviour of hard faced alloy SS304 Manuf. Sci. Technol. 2 111-115
[4]  
Baena JC(2008)Erosion behaviour of hydro turbine steels Bull. Mater. Sci. 31 115-120
[5]  
Toto A(1999)Comparison of slurry and dry erosion behaviour of some HVOF thermal sprayed coatings Wear 225 825-834
[6]  
Singh A(2014)Fe-based amorphous coatings: structures and properties Thin Solid Films 561 70-86
[7]  
Virdi RL(2009)Formation and corrosion behavior of Fe-based amorphous metallic coatings by HVOF thermal spraying Surf. Coat. Technol. 204 63-70
[8]  
Goyal K(2007)Ductile Fe-based bulk metallic glass with good soft magnetic properties Mater. Trans. 48 1157-1160
[9]  
Chauhan AK(2015)Optimization of the deposition parameters of HVOF FeMnCrSi + Ni + B thermally sprayed coatings Soldagem & Inspeção 20 238-252
[10]  
Goel DB(2014)Optimizing HVOF spray parameters to maximize bonding strength of WC–CrC–Ni coatings on AISI 304L stainless steel ASM Int. 23 860-875
12345678910