Influence of isothermal aging in LDX 2101 duplex stainless steel on the microstructure and local properties

被引:0
作者
Naima Ouali
Billel Cheniti
Brahim Belkessa
Bouzid Maamache
Ramdhane Kouba
Maamar Hakem
机构
[1] Research Center in Industrial Technologies CRTI,Laboratoire de Technologie des Matériaux, Département SDM, Faculté de Génie Mécanique et Génie des Procédés
[2] USTHB,undefined
来源
The International Journal of Advanced Manufacturing Technology | 2021年 / 116卷
关键词
Microstructure; Interface; Precipitates; Nano-hardness; Surface degradation;
D O I
暂无
中图分类号
学科分类号
摘要
In the present work, the interface morphology and the evolution of nitride precipitates in LDX 2101 stainless steel isothermally treated at 750 °C for various aging times were investigated. The microstructure results showed that the Cr2N nitrides precipitated along the δ/γ interface with 200 nm in length and continue to grow to 2 μm after 240 h of aging. However, only Cr2N nitrides were found at the δ/δ interface after long term of aging. Atomic force microscopy (AFM) analysis revealed that Cr2N nitrides and Cr23C6 carbides started to precipitate after the first 10 min of aging with a small needle shape of the former and specific triangular morphology of the latter. The evolution of hardness and Young’s modulus of the interfaces, performed with nano-indentation measurements, showed that the δ/γ interface became harder (4.1 ± 0.2 GPa) with increasing aging times, whereas negligible changes in the hardness and elastic modulus were recorded at the δ/δ interface. 3D topographic analysis of the immersed surfaces revealed that the susceptibility of δ phase to preferential dissolution in 3.5% NaCl solution increased with aging time. This behavior was manifested by the important imperfections of δ phase, the high surface roughness (55.7 nm), and the deep corrosion pits (30 nm) along the δ/γ interface and around the Cr2N nitrides.
引用
收藏
页码:1881 / 1893
页数:12
相关论文
共 168 条
  • [61] Westin EM(undefined)undefined undefined undefined undefined-undefined
  • [62] Atapour M(undefined)undefined undefined undefined undefined-undefined
  • [63] Sarlak H(undefined)undefined undefined undefined undefined-undefined
  • [64] Esmailzadeh M(undefined)undefined undefined undefined undefined-undefined
  • [65] Sathirachinda N(undefined)undefined undefined undefined undefined-undefined
  • [66] Pettersson R(undefined)undefined undefined undefined undefined-undefined
  • [67] Wessman S(undefined)undefined undefined undefined undefined-undefined
  • [68] Pan J(undefined)undefined undefined undefined undefined-undefined
  • [69] Nilsson JO(undefined)undefined undefined undefined undefined-undefined
  • [70] Wilson A(undefined)undefined undefined undefined undefined-undefined