Corrosion morphology of AZ91D exposed in an atmospheric environment

被引：0
作者：
Ye Wan
Jun Tan
Guangling Song
Chuanwei Yan
机构：
[1] Chinese Academy of Sciences,the Institute of Metals Research
[2] University of Queensland,the School of Engineering
来源：
Metallurgical and Materials Transactions A | 2006年 / 37卷
关键词：
Material Transaction; Magnesium Alloy; Corrosion Product; Atmospheric Environment; Corrosion Cavity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The focused ion beam technique was employed to investigate the atmospheric corrosion morphology of AZ91D. It was found that the α matrix of the alloy was preferentially corroded in the areas adjacent to intermetallic phases. The most interesting finding was that the corrosion products in corrosion cavities were pelletlike, which has never been reported before.
引用
收藏
页码：2313 / 2316
页数：3
相关论文
共 28 条
  • [1] Song G.(2005)undefined Adv. Eng. Mater. 7 563-563
  • [2] Song G.(2004)undefined Mater. Sci. Eng., A 336 74-74
  • [3] Bowles A.(1989)undefined Corrosion 45 741-741
  • [4] St. John D.(1993)undefined Corrosion 49 738-738
  • [5] Lunder O.(2000)undefined Corr. Sci. 42 1433-1433
  • [6] Lein J.E.(2004)undefined Corr. Sci. 46 955-955
  • [7] Aune T.K.(1997)undefined Corr. Sci. 39 1397-1397
  • [8] Nisancioglu K.(1969)undefined J. Electrochem. Soc. 116 1487-1487
  • [9] Beldjoudi T.(1996)undefined J. Electrochem. Soc. 143 2564-2564
  • [10] Fiaud C.(undefined)undefined undefined undefined undefined-undefined
123