Influence of heat treatment on microstructure and nanohardness of TiAl alloy solidified under high pressure

被引：0
作者：
Dong-dong Zhu
Duo Dong
Jie-ren Yang
Li Liu
Xiao-hong Wang
Yuan-xiang Zhang
Zun-jie Wei
机构：
[1] Quzhou University,Key Laboratory of Air
[2] Harbin Institute of Technology,driven Equipment Technology of Zhejiang Province
[3] Northwestern Polytechnical University,School of Materials Science and Engineering
来源：
China Foundry | 2020年 / 17卷
关键词：
heat treatment; TiAl; microstructure; nanohardness; TG146.23; A;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The Ti-48at.%Al alloy solidified under different pressures was prepared using a tungsten-carbide six-anvil apparatus and then heat treated at different temperatures. The effect of heat treatment on microstructure and mechanical properties of high pressure solidified Ti-48Al alloy was investigated. The results showed that the phase constitution of the Ti-48Al alloy solidified under high pressure did not change after heat treatment. After 1,100 °C/12 h AC (air cooling), the value of c/a showed a slight increase. The Widmanstätten structure was formed in the samples solidified under 2 GPa and 4 GPa. More defects were found in the high-pressure samples. The volume fraction of α2 particles increased with an increase in pressure. After 1,150 °C/4 h AC, the discontinuous coarsening phenomenon could only be found in the 4 GPa solidified samples. The formation of α2 phase can lead to the increase of nanohardness. Compared with the samples before heat treatment, the nanohardness increased about 1.0–1.2 GPa.
引用
收藏
页码：435 / 440
页数：5
相关论文
共 50 条
[41]   Heat treatment of laser metal deposited TiAl TNM alloy [J].
Rittinghaus, Silja-Katharina ;
Hecht, Ulrike ;
Werner, Valerie ;
Weisheit, Andreas .
INTERMETALLICS, 2018, 95 :94-101
[42]   Tailoring microstructure and improving oxidation resistance of an additively manufactured high Nb containing TiAl alloy via heat treatment [J].
Liang, Zhenquan ;
Xiao, Shulong ;
Yue, Hangyu ;
Li, Xinyi ;
Li, Qingchao ;
Zheng, Yunfei ;
Xu, Lijuan ;
Xue, Xiang ;
Tian, Jing ;
Chen, Yuyong .
CORROSION SCIENCE, 2023, 220
[43]   Phase Transformations Caused by Heat Treatment and High-Pressure Torsion in TiZrHfMoCrCo Alloy [J].
Gornakova, Alena S. ;
Straumal, Boris B. ;
Tyurin, Alexander I. ;
Afonikova, Natalia S. ;
Druzhinin, Alexander V. ;
Davdian, Gregory S. ;
Kilmametov, Askar R. .
MATERIALS, 2023, 16 (04)
[44]   Microstructure evolution and interfacial reaction of TiAl-Si alloy solidified in alumina crucible [J].
Fan, J. ;
Guo, J. ;
Wang, S. ;
Tian, S. ;
Su, Y. ;
Liu, J. ;
Fu, H. .
MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (14) :1727-1734
[45]   Effect of aging treatment on properties of Al-Si alloy solidified at high-pressure [J].
Huang, Haosheng ;
Jiang, Bo ;
Jiang, Wentao ;
Wang, Ye ;
Zhu, Dongdong ;
Hu, Maoliang .
MATERIALS SCIENCE AND TECHNOLOGY, 2023, 39 (15) :1999-2005
[46]   Microstructure and mechanical properties of an Al-Mg alloy solidified under high pressures [J].
Jie, J. C. ;
Zou, C. M. ;
Brosh, E. ;
Wang, H. W. ;
Wei, Z. J. ;
Li, T. J. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 578 :394-404
[47]   Pilot processing and microstructure control of high Nb containing TiAl alloy [J].
Xu, XJ ;
Xu, LH ;
Lin, JP ;
Wang, YL ;
Lin, Z ;
Chen, GL .
INTERMETALLICS, 2005, 13 (3-4) :337-341
[48]   Structure and Properties of Silumin Castings Solidified Under Pressure After Heat Treatment [J].
Stancek, L. ;
Vanko, B. ;
Batyshev, A. I. .
METAL SCIENCE AND HEAT TREATMENT, 2014, 56 (3-4) :197-202
[49]   The effect of process parameters and heat treatment on the microstructure of direct laser fabricated TiAl alloy samples [J].
Srivastava, D ;
Chang, ITH ;
Loretto, MH .
INTERMETALLICS, 2001, 9 (12) :1003-1013
[50]   Structure and Properties of Silumin Castings Solidified Under Pressure After Heat Treatment [J].
L. Stanček ;
B. Vanko ;
A. I. Batyshev .
Metal Science and Heat Treatment, 2014, 56 :197-202
12345