Electrical properties of Na2SO4-based composite systems

被引：0
作者：
S. M. Bobade
A. R. Kulkarni
P. Gopalan
机构：
[1] Indian Institute of Technology Bombay,Department of Metallurgical Engineering and Materials Science
来源：
Ionics | 2007年 / 13卷
关键词：
Composite electrolytes; Na; conductors; Ionic conductivities;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Composite electrolytes are well-known multiphase systems and exhibit maxima in the conductivity at certain second-phase concentration. An attempt has been made to investigate a number of sodium sulfate (Na2SO4)-based composite systems. The dispersoids that have been used are MgO, Al2O3, and SiO2. The samples have been characterized using impedance spectroscopy, X-ray diffraction, and differential scanning calorimetry. The maximum conductivity has been observed for MgO dispersed system, and the percolation threshold has been observed at 30-mol% dispersoid, MgO concentration. Interestingly, two maxima have been observed in case of the Na2SO4–SiO2 and Na2SO4–Al2O3 composite systems. In the Na2SO4–SiO2 system, the first maximum occurs at lower concentration, i.e., in the range between 10 and 20 mol%, whereas the second occurs at the 40-mol% dispersoid concentration. For the Na2SO4–Al2O3 system, although slightly indistinguishable, two peaks in the conductivity vs composition plot have been observed around 12- and 30-mol% Al2O3 concentrations.
引用
收藏
页码：257 / 262
页数：5
相关论文
共 78 条
[1]  
Liang CC(1973)undefined J Electrochem Soc 128 1289-undefined
[2]  
Jain A(2000)undefined Mater Res Bull 35 2337-undefined
[3]  
Saha S(2000)undefined J Solid State Chem 153 287-undefined
[4]  
Gopalan P(1985)undefined Amer Ceram Soc 68 538-undefined
[5]  
Kulkarni AR(1989)undefined Ann Rev Mater Sci 19 103-undefined
[6]  
Jain A(2000)undefined J Solid State Chem 155 154-undefined
[7]  
Saha S(1995)undefined Prog Solid State Chem 23 171-undefined
[8]  
Gopalan P(1981)undefined Solid State Ionics 3/4 295-undefined
[9]  
Kulkarni AR(1992)undefined Solid State Ionics 51 41-undefined
[10]  
Dudney NJ(1994)undefined Solid State Ionics 74 15-undefined
12345678