Effect of the microstructure on the mechanical properties of a directionally solidified Y3Al5O12/Al2O3 eutectic fiber

被引：0
作者：
D.-Y. Park
J.-M. Yang
机构：
[1] University of California,Department of Materials Science and Engineering
来源：
Journal of Materials Science | 2001年 / 36卷
关键词：
Microstructure; Scanning Electron Microscopy; Heat Treatment; Tensile Strength; Fracture Toughness;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The strength and fracture behaviors of a directionally solidified Y3Al5O12/Al2O3 eutectic fiber were investigated. The fiber was grown continuously by an edge-defined film-fed growth (EFG) technique. The microstructure was characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The room temperature tensile strength and Weibull's modulus of the eutectic fiber before and after heat treatment at 1460°C were measured. The fracture toughness and crack propagation behaviors were investigated using an indentation technique. Significant coarsening of the lamellar microstructure was observed after heat treatment at 1460°C in air. The degradation of the room temperature tensile strength in the Y3Al5O12/Al2O3 eutectic fiber after heat treatment was attributed to the development of surface grooves at the surface of the fiber. Also, the Y3Al5O12/Al2O3 eutectic fiber showed a radial (Palmqvist) crack type and exhibited an anisotropic crack propagation behavior during the indentation tests.
引用
收藏
页码：5593 / 5601
页数：8
相关论文
共 50 条
[1]   Mechanical properties of directionally solidified Al2O3/Y3Al5O12 eutectic ceramic prepared by optical floating zone technique [J].
Wang, Xu ;
Tian, Zhilin ;
Zhang, Wen ;
Zhong, Yujie ;
Xian, Quangang ;
Zhang, Jian ;
Wang, Jingyang .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2018, 38 (10) :3610-3617
[2]   Microstructure and mechanical properties of a directionally solidified Al2O3/Y3Al5O12/ZrO2 hypoeutectic in situ composite [J].
Su, Haijun ;
Zhang, Jun ;
Liu, Lin ;
Fu, Hengzhi .
COMPOSITES SCIENCE AND TECHNOLOGY, 2009, 69 (15-16) :2657-2667
[3]   Fracture morphology and mechanism of a directionally solidified Al2O3/Y3Al5O12 eutectic single crystal [J].
Wang, Xu ;
Zhong, Yujie ;
Wang, Dong ;
Xian, Quangang ;
Wang, Jingyang ;
Lou, Langhong ;
Zhang, Jian .
SCRIPTA MATERIALIA, 2017, 135 :46-49
[4]   A modified preparation technique and characterization of directionally solidified Al2O3/Y3Al5O12 eutectic in situ composites [J].
Su, Haijun ;
Zhang, Jun ;
Deng, Yangfang ;
Liu, Lin ;
Fu, Hengzhi .
SCRIPTA MATERIALIA, 2009, 60 (06) :362-365
[5]   Crystallography and interfacial structure in a directionally solidified Al2O3/Y3Al5O12/ZrO2 eutectic crystal [J].
Wang, Xu ;
Zhong, Yujie ;
Sun, Qian ;
Li, Yiran ;
Zhang, Wen ;
Qi, Dongqing ;
Wang, Dong ;
Jiang, Bailing .
SCRIPTA MATERIALIA, 2018, 145 :23-27
[6]   Microstructure and mechanical properties of Al2O3/Y3Al5O12/ZrO2 hypereutectic directionally solidified ceramic prepared by laser floating zone [J].
Song, Kan ;
Zhang, Jun ;
Lin, In ;
Liu, Lin ;
Huang, Weidong .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (12) :3051-3059
[7]   Preparation and microstructure of large-sized directionally solidified Al2O3/Y3Al5O12 eutectics with the seeding technique [J].
Wang, Xu ;
Zhang, Wen ;
Xian, Quangang ;
Shen, Jian ;
Zhang, Gong ;
Wang, Dong ;
Wang, Jingyang ;
Lou, Langhong ;
Zhang, Jian .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2018, 38 (16) :5625-5631
[8]   Microstructure of Al2O3/Y3Al5O12 eutectic fibers grown by μ-PD method [J].
Epelbaum, BM ;
Yoshikawa, A ;
Shimamura, K ;
Fukuda, T ;
Suzuki, K ;
Waku, Y .
JOURNAL OF CRYSTAL GROWTH, 1999, 198 :471-475
[9]   Fracture behavior of directionally solidified CeO2- and Pr2O3-doped Y3Al5O12/Al2O3 eutectic composites [J].
Park, DY ;
Yang, JM .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 332 (1-2) :276-284
[10]   Processing, microstructure, and properties of laser remelted Al2O3/Y3Al5O12(YAG) eutectic in situ composite [J].
Su Hai-jun ;
Zhang Jun ;
Liu Lin ;
Fu Heng-zhi .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 (06) :1259-1264
12345