Mechanochemical processing of nanocrystalline Ti-6Al-4V alloy

被引：1
作者：
M. D. S. Pirzada
F. H. (Sam) Froes
S. N. Patankar
机构：
[1] the University of Idaho,Department of Materials and Metallurgical Engineering
[2] the University of Idaho,Institute for Materials and Advanced Processes
来源：
Metallurgical and Materials Transactions A | 2004年 / 35卷
关键词：
Milling; Material Transaction; Dehydrogenation; Powder Mixture; Ignition Time;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Synthesis of nanocrystalline Ti-6Al-4V was explored using mechanochemical processing. The reaction mixture was comprised of CaH2, Mg powder, anhydrous AlCl3, anhydrous VCl3, and TiCl4. The milled powder (reaction product) primarily consisted of nanocrystalline alloy hydride having a composition (Ti-6Al-4V)H1.942, along with MgCl2 and CaCl2 as by-products. Aqueous solutions of nitric acid, sulfuric acid, and 1 pct sodium sulfite were found to be very effective in leaching of the chlorides from the milled powder. The (Ti-6Al-4V)H1.942 on dehydrogenation at 375°C resulted in nanocrystalline Ti-6Al-4V alloy powder.
引用
收藏
页码：1899 / 1903
页数：4
相关论文
共 50 条
  • [31] Measurement and analysis of pocket milling features in abrasive water jet machining of Ti-6Al-4V alloy
    Natarajan, Yuvaraj
    Raj, K. L. Naresh
    Tandon, Puneet
    [J]. ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2022, 23 (01)
  • [32] Effects of microstructural morphology on quasi-static and dynamic deformation behavior of Ti-6Al-4V alloy
    Dong-Geon Lee
    Sangho Kim
    Sunghak Lee
    Chong Soo Lee
    [J]. Metallurgical and Materials Transactions A, 2001, 32 : 315 - 324
  • [33] Investigating the microstructure and morphology of chips in dry, flood coolant and MQL machining of Ti-6Al-4V alloy
    Khatri A.
    Jahan M.P.
    [J]. International Journal of Sustainable Manufacturing, 2020, 4 (2-4) : 234 - 250
  • [34] Mechanism of surface modification of the Ti-6Al-4V alloy using a gas tungsten arc heat source
    M. Labudovic
    R. Kovacevic
    I. Kmecko
    T. I. Khan
    D. Blecic
    Z. Blecic
    [J]. Metallurgical and Materials Transactions A, 1999, 30 : 1597 - 1603
  • [35] Quantification of Microstructural Features and Prediction of Mechanical Properties of a Dual-Phase Ti-6Al-4V Alloy
    Yang, Dong
    Liu, Zhanqiang
    [J]. MATERIALS, 2016, 9 (08):
  • [36] Experimental Investigations into the Effects of Microelectric-Discharge Milling Process Parameters on Processing Ti-6Al-4V
    Kuriachen, B.
    Mathew, J.
    [J]. MATERIALS AND MANUFACTURING PROCESSES, 2015, 30 (08) : 983 - 990
  • [37] Durability of Fe-Co thin films on Ti-6Al-4V
    K. S. Chan
    S. J. Hudak
    C. E. Smith
    G. M. Light
    B. R. Lanning
    A. Veit
    [J]. Metallurgical and Materials Transactions A, 2006, 37 : 1443 - 1457
  • [38] Cavitation during hot-torsion testing of Ti-6Al-4V
    P. D. Nicolaou
    J. D. Miller
    S. L. Semiatin
    [J]. Metallurgical and Materials Transactions A, 2005, 36 : 3461 - 3470
  • [39] Analysis of Microstructure and Chip Formation When Machining Ti-6Al-4V
    Shyha, Islam
    Gariani, Salah
    El-Sayed, Mahmoud Ahmed
    Huo, Dehong
    [J]. METALS, 2018, 8 (03)
  • [40] Mechanisms of globularization of Ti-6Al-4V during static heat treatment
    N. Stefansson
    S. L. Semiatin
    [J]. Metallurgical and Materials Transactions A, 2003, 34 : 691 - 698
12345