Mechanochemical processing of nanocrystalline Ti-6Al-4V alloy

被引：0
作者：
M. D. S. Pirzada
F. H. (Sam) Froes
S. N. Patankar
机构：
[1] the University of Idaho,Department of Materials and Metallurgical Engineering
[2] the University of Idaho,Institute for Materials and Advanced Processes
来源：
Metallurgical and Materials Transactions A | 2004年 / 35卷
关键词：
Milling; Material Transaction; Dehydrogenation; Powder Mixture; Ignition Time;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Synthesis of nanocrystalline Ti-6Al-4V was explored using mechanochemical processing. The reaction mixture was comprised of CaH2, Mg powder, anhydrous AlCl3, anhydrous VCl3, and TiCl4. The milled powder (reaction product) primarily consisted of nanocrystalline alloy hydride having a composition (Ti-6Al-4V)H1.942, along with MgCl2 and CaCl2 as by-products. Aqueous solutions of nitric acid, sulfuric acid, and 1 pct sodium sulfite were found to be very effective in leaching of the chlorides from the milled powder. The (Ti-6Al-4V)H1.942 on dehydrogenation at 375°C resulted in nanocrystalline Ti-6Al-4V alloy powder.
引用
收藏
页码：1899 / 1903
页数：4
相关论文
共 50 条
  • [21] Thermomechanical response of a powder metallurgy Ti-6Al-4V alloy modified with 2.9 pct boron
    Radhakrishna B. Bhat
    Seshacharyulu Tamirisakandala
    Daniel B. Miracle
    Vilupanur A. Ravi
    Metallurgical and Materials Transactions A, 2005, 36 : 845 - 857
  • [22] Effect of cutting parameters on machining surface and cutting tool in milling of Ti-6Al-4V alloy
    Celik, Yahya Hisman
    Karabiyik, Ahmet
    INDIAN JOURNAL OF ENGINEERING AND MATERIALS SCIENCES, 2016, 23 (05) : 349 - 356
  • [23] Thermomechanical response of a powder metallurgy Ti-6Al-4V alloy modified with 2.9 pct boron
    Bhat R.B.
    Tamirisakandala S.
    Miracle D.B.
    Ravi V.A.
    Metallurgical and Materials Transactions A, 2005, 36 (13) : 845 - 857
  • [24] Investigation of wear during cryogenic machining of Ti-6Al-4V
    Gutzeit K.
    Basten S.
    Kirsch B.
    Aurich J.C.
    ZWF Zeitschrift fuer Wirtschaftlichen Fabrikbetrieb, 2021, 116 (09): : 599 - 602
  • [25] Machining of GTAW additively manufactured Ti-6Al-4V structures
    N. Hoye
    D. Cuiuri
    R. A. Rahman Rashid
    S. Palanisamy
    The International Journal of Advanced Manufacturing Technology, 2018, 99 : 313 - 326
  • [26] Diffusion coefficients for modeling the heat treatment of Ti-6Al-4V
    S. L. Semiatin
    T. M. Brown
    T. A. Goff
    P. N. Fagin
    R. E. Turner
    J. M. Murry
    D. R. Barker
    J. D. Miller
    F. Zhang
    Metallurgical and Materials Transactions A, 2004, 35 : 3015 - 3018
  • [27] Cavitation and failure during hot forging of Ti-6Al-4V
    S. L. Semiatin
    R. L. Goetz
    V. Seetharaman
    E. B. Shell
    A. K. Ghosh
    Metallurgical and Materials Transactions A, 1999, 30 : 1411 - 1424
  • [28] Machining of GTAW additively manufactured Ti-6Al-4V structures
    Hoye, N.
    Cuiuri, D.
    Rashid, R. A. Rahman
    Palanisamy, S.
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 99 (1-4) : 313 - 326
  • [29] Creep expansion of porous Ti-6Al-4V sandwich structures
    Douglas T. Queheillalt
    Haydn N. G. Wadley
    Bill W. Choi
    Daniel S. Schwartz
    Metallurgical and Materials Transactions A, 2000, 31 : 261 - 273
  • [30] Diffusion coefficients for modeling the heat treatment of Ti-6Al-4V
    Semiatin, SL
    Brown, TM
    Goff, TA
    Fagin, PN
    Barker, DR
    Turner, RE
    Murry, JM
    Miller, JD
    Zhang, F
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (09): : 3015 - 3018
12345