Dry pressing boehmite gels for the fabrication of monolithic α-Al2O3

被引：1
|
作者：
Seongtae Kwon
Gary L. Messing
机构：
[1] Pennsylvania State University,Department of Materials Science and Engineering, The Particulate Materials Center
来源：
Journal of Sol-Gel Science and Technology | 1997年 / 9卷 / 1期
关键词：
boehmite gel; agglomerates; dry pressing; sintering; alumina;
D O I：
10.1007/BF02439336
中图分类号：
学科分类号：
摘要：
It is demonstrated that dense alpha alumina can be fabricated by pressing ethanol-dispersed, α-Al2O3 seeded boehmite. Green bodies were formed by uniaxially pressing either water or ethanol dispersed gel powder and then isostatically pressing the compacts at 280 MPa. Green microstructure and alumina densification are correlated with gel agglomerate size and dispersing medium. The ethanol-dispersed specimens showed better sinterability than the water-dispersed specimens, and sintered to more than 99% theoretical density at 1300°C. It is shown that softer gel agglomerates were obtained by alcohol dispersion and resulted in better green microstructure and higher sintered density.
引用
收藏
页码：53 / 64
页数：11
相关论文
共 50 条
  • [31] Fabrication of Al2O3 ceramics by environmentally friendly process
    Nagaoka, Takaaki
    Tsugoshi, Takahisa
    Hotta, Yuji
    Sato, Kimiyasu
    Watari, Koji
    SCIENCE OF ENGINEERING CERAMICS III, 2006, 317-318 : 751 - 754
  • [32] Simulation of Fabrication for Al2O3 Ceramic Tool Materials
    Fang, Bin
    Huang, Chuanzhen
    Zhu, Hongtao
    Xu, Chonghai
    ADVANCES IN MATERIALS PROCESSING X, 2012, 500 : 537 - +
  • [33] Utilization of Al scrap for fabrication of Al(alloy)/Al2O3 composite material
    Yoshikawa, N
    Yamaguchi, H
    Kitahara, G
    Taniguchi, S
    MATERIALS TRANSACTIONS, 2003, 44 (07) : 1271 - 1275
  • [34] Consolidated Al/Al2O3 Nanocomposites by Equal Channel Angular Pressing and Hot Extrusion
    Casati, Riccardo
    Vedani, Maurizio
    Dellasega, David
    Bassani, Paola
    Tuissi, Ausonio
    MATERIALS AND MANUFACTURING PROCESSES, 2015, 30 (10) : 1218 - 1222
  • [35] Sintering of α-Al2O3 nanocrystalline ceramic from large α-Al2O3 polycrystalline nanoparticles
    Cao, Wenbin
    Mao, Xuan
    Li, Lu
    Wang, Bing
    Guo, Qian
    Li, Jiangong
    CERAMICS INTERNATIONAL, 2017, 43 (01) : 1378 - 1382
  • [36] Sintering behaviour and microstructures of Ti(Al,O)/Al2O3, Ti3Al(O)/Al2O3 and TiAl(O)/Al2O3 in situ composites
    Cai, ZH
    Zhang, DL
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 419 (1-2): : 310 - 317
  • [37] Preparation of Pseudo-boehmite and γ-Al2O3 by Polyaluminum Chloride II -Surfactant Influences
    Wang Yuan-Yuan
    Zhao Chang-Wei
    He Jin-Song
    Yan Yong
    Zhang Xiang-Lan
    Luan Zhao-Kun
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2012, 28 (02) : 302 - 306
  • [38] Fabrication and characterisation of bulk Al2O3/Mo nanocomposite by mechanical milling and sintering
    Heidarpour, A.
    Karimzadeh, F.
    Enayati, M. H.
    POWDER METALLURGY, 2011, 54 (04) : 513 - 517
  • [39] Plasma-reduced Ni/γ-Al2O3 and CeO2-Ni/γ-Al2O3 catalysts for improving dry reforming of propane
    Karuppiah, J.
    Mok, Young Sun
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2014, 39 (29) : 16329 - 16338
  • [40] Capabilities of α-Al2O3, γ-Al2O3, and bentonite dry powders used in flat plate solar collector for thermal energy storage
    Akbarzadeh, Alireza
    Ahmadlouydarab, Majid
    Niaei, Aligholi
    RENEWABLE ENERGY, 2021, 173 : 704 - 720
12345