Refractory Corrosion Resistance in Molten Lead-Niobium Glass

被引：0
作者：
V. A. Sokolov
M. D. Gasparyan
机构：
[1] FGAOU VO NITU MISiS,
[2] OOO TsIT SPETsKEROKOM,undefined
来源：
Refractories and Industrial Ceramics | 2018年 / 59卷
关键词：
lead-niobium glass; sitalls; platinum crucible; corrosion resistance; chromium-containing refractory; glass melting furnace;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
It is shown that chromium-containing refractories containing more than 80% Cr2O3 are most corrosion-resistant in molten lead-niobium glass at 1440°C. Alongside good corrosion resistance fusion-cast high-chromium refractories are capable of providing prescribed glass electrophysical properties, obtained on contact with chromium refractory. The data provided point to the possibility of replacing platinum melting equipment during preparation of lead-niobium glass with use of a small bath electric melting furnace with a lining of fusion-cast high-chromium refractory.
引用
收藏
页码：223 / 226
页数：3
相关论文
共 5 条
  • [1] Blokhina GP(1987)Effect of glass phase composition on the structure and properties of condenser sitalls based on a solid solution of lead-barium-strontium niobate and titanate solid solutions Neorgan. Materialy 23 1377-1381
  • [2] Dukarevich NY(2005)The structure of fusion-cast high-chrome oxide refractories in the Cr Refract. Indust. Ceram. 46 127-131
  • [3] Naumova TA(undefined)O undefined undefined undefined-undefined
  • [4] Sokolov VA(undefined)–MgO–Al undefined undefined undefined-undefined
  • [5] Malysheva TY(undefined)O undefined undefined undefined-undefined
1