Study of the Specifics of Liquid-Phase Oxidation of Aluminum Melt to Obtain an Aluminum Matrix Composite

被引：0
作者：
A. D. Romanov
E. A. Romanova
E. A. Chernyshov
机构：
[1] Federal State Budgetary Educational Institution of Higher Education “Nizhny Novgorod State Technical University”,
来源：
Metallurgist | 2021年 / 65卷
关键词：
aluminum oxide (alumina); aluminum; composite material; mechanical properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The paper describes theoretical studies and presents the results of practical experiments related to the production of aluminum matrix composites by internal oxidation. According to the proposed technology, the formation of aluminum oxide occurs directly inside the aluminum melt, which enables a one-step process for producing a composite material and also ensures the economic efficiency of the process. The theoretical part discusses the basic provisions of the model of internal liquid-phase oxidation of molten aluminum with oxygen to produce α-Al2O3. The practical part provides the results of mechanical tests as well as sample microstructure, which confirm the theoretical assumptions. The possibility of achieving various levels of melt saturation as well as a wide range of various strengthening phase sizes has been shown. The porosity of the resulting material was analyzed. A comparative cost analysis of the alloys produced by adding Al2O3 powder and by utilizing internal oxidation of molten aluminum was performed.
引用
收藏
页码：775 / 782
页数：7
相关论文
共 34 条
  • [1] Koli DK(2013)Properties and characterization of Al-Al Int. J. of Latest Trends in Engineering and Technology (IJLTET) 2 486-493
  • [2] Agnihotri G(2011)O Int. J. of Automotive and Mechanical Engineering 4 471-480
  • [3] Purohit R(2004) composites processed by casting and powder metallurgy routes (review) Wear 256 275-285
  • [4] Adebisi AA(1988)Metal matrix composite brake rotor: historical development and product life cycle analysis JOM 40 12-19
  • [5] Maleque MA(2015)High temperature friction and wear behavior of Al Novosti Materialovedeniya. Nauka i Tekhnika 3 3-10
  • [6] Rahman MM(2015)O Novosti Materialovedeniya. Nauka i Tekhnika 3 11-17
  • [7] Yao-Hui L(2016) and/or carbon short fiber reinforced Al-12Si alloy composites American J. of Mater. Sci. 6 99-101
  • [8] Jun D(2018)Solidification processing of metal matrix composites Mater. and Manufacturing Processes 33 1313-1323
  • [9] Si-Rong Y(2014)Specifics of using a structural metallic composite material based on SiC particle-reinforced aluminum alloy. Part I (review) Atlas J. Mater. Sci. 1 30-37
  • [10] Wei W(undefined)Specifics of using a structural metallic composite material based on SiC particle-reinforced aluminum alloy. Part II (review) undefined undefined undefined-undefined
1234