Cavitation Erosion Behavior of Nb Strengthened Duplex Stainless Steel Surfacing Layer

被引：0
作者：
Yefeng Bao
Chong Cao
Bingqi Xie
Zirui Wang
Linpo Guo
Ke Yang
Qining Song
机构：
[1] Hohai University,College of Mechanical and Electrical Engineering
[2] Fujian Fuqing Nuclear Power Co. Ltd,undefined
来源：
Journal of Materials Engineering and Performance | 2022年 / 31卷
关键词：
cavitation erosion; duplex stainless steel; mechanical properties; Nb; solid solution strengthening;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this paper, the Nb-containing duplex stainless steel (DSS) was prepared using the tungsten inert-gas welding powder surfacing method, and the solution treatment was carried out at different temperatures. A scanning electron microscope with an energy-dispersive spectrometer, universal testing machine, and ultrasonic cavitation equipment were used to study the structure, mechanical properties, and cavitation erosion (CE) resistance of DSS. The results showed that, compared with the as-welded 2209 DSS, Nb-containing DSS has better strength and lower plasticity. After heat treatment, the strength and plasticity of Nb-containing DSS were also reduced. During the ultrasonic CE test, the cumulative weight losses of the Nb-containing DSSs for 6 h were less than that of the control group (2209 DSS). However, solution treatment caused the Z phase to appear in the Nb-containing DSSs. Z phase reduced the mechanical properties of the matrix, promoted the initiation of CE cracks, and increased the cavitation weight loss of the sample after heat treatment.
引用
收藏
页码：10367 / 10377
页数：10
相关论文
共 149 条
[1]  
Espitia LA(2010)Cavitation Resistance, Microstructure and Surface Topography of Materials Used for Hydraulic Components [J] Tribol. Int. 43 2037-2045
[2]  
Toro A(2020)Synergistic Effect between Cavitation Erosion and Corrosion for Various Copper Alloys in Sulphide-Containing 3.5% NaCl Solutions Wear 450–451 203258-31
[3]  
Song QN(2012)Synergy of Cavitation and Slurry Erosion in the Slurry Pot Tester Wear 290–291 25-240
[4]  
Tong Y(2021)Dual Role of microparticles in Synergistic Cavitation–Particle Erosion: Modeling and experiments Wear 470–471 203633-369
[5]  
Xu N(1966)The Collapse of Cavitation Bubbles and the Pressures thereby Produced against Solid Boundaries. Philosophical transactions of the Royal Society of London Ser. A: Math. Phys. Sci. 260 221-759
[6]  
Sun SY(2022)Corrosion and Cavitation Erosion Resistance Enhancement of Cast Ni-Al Bronze by Laser Surface Melting J. Iron. Steel Res. Int. 29 359-184
[7]  
Li HL(2015)Cavitation Erosion Behavior of Hastelloy C-276 Nickel-Based Alloy J. Alloy. Compd. 619 754-271
[8]  
Bao YF(1983)Cavitational Damage of Titanium in Molten Lead Bull. Mater. Sci. 5 179-75
[9]  
Jiang YF(1997)The Process (Mechanism) of Erosion of Soluble Brittle Materials Caused by Cavitation Ultrason. Sonochem. 4 269-716
[10]  
Wang ZB(1991)Erosion and Corrosion of Cast Iron under Cavitation Conditions Tribol. Int. 24 67-2420
12345678910