Preparation of La0.75Sr0.25MnO3 Nano-Phase Powders and Films from Alkoxide Precursors

被引:1
作者
Annika Pohl
Gunnar Westin
Kjell Jansson
机构
来源
Journal of Sol-Gel Science and Technology | 2003年 / 26卷
关键词
film; La; Sr; MnO; nano-phase powder; sol-gel; thermal phase; evolution studies;
D O I
暂无
中图分类号
学科分类号
摘要
The first purely alkoxide-based sol-gel route to nano-phase powders and thin films of perovskite La0.75Sr0.25MnO3 is described. The phase and microstructure evolution on heat treatment of free gel films to form the target nano-phase oxide were investigated by TGA, IR spectroscopy, powder XRD, SEM and TEM-EDS. The xerogel consisted of a hydrated oxo-carbonate, without remaining alkoxo groups or solvent. Heating at 5°C·min−1 decomposed the carbonate groups and yielded the pure perovskite La0.75Sr0.25MnO3 at 760°C. The cell dimensions were virtually unchanged from the first observation of perovskite at 680°C, to 1000°C, 4 h. The monoclinic cell of La0.75Sr0.25MnO3 obtained at 1000°C, 4 h, had the dimensions a = 5.475(1), b = 5.504(2), c = 7.771(1) Å, β = 90.50(2), fitting the literature data quite well. Crack-free, homogenous, 150 nm thick La0.75Sr0.25MnO3 films were prepared by spin-coating Si/SiO2/TiO2/Pt and polycrystalline α-Al2O3 substrates with a 0.6 M alkoxide solution, followed by heating at 5°C·min−1 to 800°C, 30 min.
引用
收藏
页码:257 / 260
页数:3
相关论文
empty
未找到相关数据