The grafting of recycled polyol from waste polyurethane foam onto new polyurethane and its impact on shape recovery and water vapor permeation

Recycled polyols from waste polyurethane (PU) foams were grafted onto PU to improve the properties such as tensile strength, shape recovery, low-temperature flexibility, and water compatibility. The recycled polyol was either purified by column chromatography before grafting or was used directly for grafting. The soft segment melting temperature of PU did not notably increase with the addition of polyol, whereas the glass transition temperature increased with increased polyol content. The tensile strength sharply increased at low polyol content and decreased at high polyol content, while the strain at break did not significantly change with an increase in polyol content. The shape recovery at 10 oC notably improved compared with unmodified PU and remained high after four cyclic tests. Polyol-grafted PU demonstrated better lowtemperature flexibility and reduced the water vapor permeability of PU membranes. Overall, grafting recycled polyol onto PU significantly improved the tensile stress, shape recovery, and low-temperature flexibility of PU.