High-Dose Phosphorus-Implanted 4H-SiC: Microwave and Conventional Post-Implantation Annealing at Temperatures ≥1700°C

Semi-insulating 4H-SiC ⟨0001⟩ wafers have been phosphorus ion implanted at 500°C to obtain phosphorus box depth profiles with dopant concentration from 5 × 1019 cm−3 to 8 × 1020 cm−3. These samples have been annealed by microwave and conventional inductively heated systems in the temperature range 1700°C to 2050°C. Resistivity, Hall electron density, and Hall mobility of the phosphorus-implanted and annealed 4H-SiC layers have been measured in the temperature range from room temperature to 450°C. The high-resolution x-ray diffraction and rocking curve of both virgin and processed 4H-SiC samples have been analyzed to obtain the sample crystal quality up to about 3 μm depth from the wafer surface. For both increasing implanted phosphorus concentration and increasing post-implantation annealing temperature the implanted material resistivity decreases to an asymptotic value of about 1.5 × 10−3 Ω cm. Increasing the implanted phosphorus concentration and post-implantation annealing temperature beyond 4 × 1020 cm−3 and 2000°C, respectively, does not bring any apparent benefit with respect to the minimum obtainable resistivity. Sheet resistance and sheet electron density increase with increasing measurement temperature. Electron density saturates at 1.5 × 1020 cm−3 for implanted phosphorus plateau values ≥4 × 1020 cm−3, irrespective of the post-implantation annealing method. Implantation produces an increase of the lattice parameter in the bulk 4H-SiC underneath the phosphorus-implanted layer. Microwave and conventional annealing produce a further increase of the lattice parameter in such a depth region and an equivalent recovered lattice in the phosphorus-implanted layers.