The effect of surface treatments on interfacial fatigue crack initiation in aluminum/epoxy bonds

被引：0
作者：
D.R. Lefebvre
B.K. Ahn
D.A. Dillard
J.G. Dillard
机构：
[1] Virginia Polytechnic Institute and State University,Center for Adhesive and Sealant Science
[2] Motorola,undefined
[3] Pacific Northwest National Laboratory,undefined
[4] Department of Engineering Science and Mechanics,undefined
[5] Department of Chemistry,undefined
来源：
International Journal of Fracture | 2002年 / 114卷
关键词：
Adhesive bonds; aluminum/epoxy bonds; bimaterial interfaces; fatigue crack initiation; phosphoric acid anodization; P2 etch; stress singularities; pre-treatment; sol-gel; sulfuric acid anodization.;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of different substrate surface pre-treatments on the initiation of interfacial fatigue cracks was studied for adhesive bonds. Aluminum-epoxy bimaterial specimens were used to investigate how surface pre-treatment affects resistance to fatigue crack initiation at the interface corner. A stress singularity approach was utilized to assess the effect of four different treatments; P2 etch, phosphoric acid anodization (PAA), sulfuric acid anodization (SAA), and sol-gel. A bimaterial system with a 90° epoxy wedge was tested under sinusoidal cyclic loading. The surface treatment effect was rather significant on the resistance to fatigue crack initiation at the interface. Results show that PAA generated the strongest interface, while SAA led to the weakest for the material system studied here.
引用
收藏
页码：191 / 202
页数：11
相关论文
共 50 条
[31]   Effect of microstructure on small fatigue crack initiation and early propagation behavior in super martensite stainless steel [J].
Li, Xue ;
Ye, Tian ;
Du, Yaohan ;
Zhan, Min ;
Wang, Xiangyu ;
Dai, Yajun ;
Liu, Yongjie ;
Wang, Chong ;
Yang, Kun ;
He, Chao ;
Wang, Qingyuan .
INTERNATIONAL JOURNAL OF FATIGUE, 2025, 190
[32]   Effect of microstructure inhomogeneity and crack initiation environment on the very high cycle fatigue behavior of a magnesium alloy [J].
Chen, Yao ;
He, Chao ;
Liu, Fulin ;
Wang, Chong ;
Xie, Qing ;
Wang, Qingyuan ;
Liu, Yongjie .
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 131
[33]   On the physical interpretation of the R-ratio effect and the LEFM parameters used for fatigue crack growth in adhesive bonds [J].
Pascoe, J. A. ;
Alderliesten, R. C. ;
Benedictus, R. .
INTERNATIONAL JOURNAL OF FATIGUE, 2017, 97 :162-176
[34]   Crystal plasticity modeling of microstructure influence on fatigue crack initiation in extruded A16082-T6 with surface irregularities [J].
Hallberg, Hakan ;
As, Sigmund Kyrre ;
Skallerud, Bjorn .
INTERNATIONAL JOURNAL OF FATIGUE, 2018, 111 :16-32
[35]   The effect of crystallographic orientation and grain boundary misorientation on dwell fatigue crack initiation in a near-α titanium alloy [J].
Zhou, Honggen ;
Zhou, Rong ;
Sun, Guanze ;
Zhao, Zihua .
INTERNATIONAL JOURNAL OF FATIGUE, 2025, 200
[36]   A Methodology for Incorporating the Effect of Grain Size on the Energy Efficiency Coefficient for Fatigue Crack Initiation Estimation in Polycrystalline Metal [J].
Ou, Chun-Yu ;
Voothaluru, Rohit ;
Liu, C. Richard .
METALS, 2020, 10 (03)
[37]   Effect of Notches on Fatigue Crack Initiation and Early Propagation Behaviors of a Ni-Based Superalloy at Elevated Temperatures [J].
Zhao, Zuopeng ;
Hu, Xuteng ;
Guo, Zhiwei .
METALS, 2025, 15 (04)
[38]   Multi-dimensional study of the effect of early slip activity on fatigue crack initiation in a near-? titanium alloy [J].
Liu, Conghui ;
Thomas, Rhys ;
Sun, Tianzhu ;
Donoghue, Jack ;
Zhang, Xun ;
Burnett, Tim L. ;
Fonseca, Joao Quinto da ;
Preuss, Michael .
ACTA MATERIALIA, 2022, 233
[39]   Effect of microstructure on slip-induced crack initiation and early propagation of martensitic steel during high cycle fatigue [J].
Dai, Yajun ;
Wang, Shijian ;
He, Qiyuan ;
Liu, Chang ;
Wang, Xianyu ;
Li, Xue ;
Li, Lang ;
Liu, Yongjie ;
He, Chao ;
Wang, Qingyuan .
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 167
[40]   Al-Li alloy AA2198's very high cycle fatigue crack initiation mechanism and its fatigue thermal effect [J].
Xu, Luopeng ;
Cao, Xiaojian ;
Chen, Yu ;
Wang, Qingyuan .
AOPC 2015: OPTICAL TEST, MEASUREMENT, AND EQUIPMENT, 2015, 9677
12345