Improving characteristics of melamine–urea–formaldehyde resin by addition of blocked polyurethane prepolymer

被引：0
作者：
Jun Jiang
Xiaoning Lu
机构：
[1] Beijing Forestry University,College of Materials Science and Technology
[2] Nanjing Forestry University,College of Materials Science and Engineering
来源：
European Journal of Wood and Wood Products | 2017年 / 75卷
关键词：
Contact Angle; Moisture Content; Melamine; Fiber Saturation Point; Equilibrium Contact Angle;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this paper, the effect of blocked polyurethane prepolymer (BPUP) with four R values (the ratio of –NCO to –OH) and different blending proportions on the characteristics of melamine–urea–formaldehyde (MUF) resin were first investigated. The properties of the modified adhesive systems were examined by dynamic wettability and shear strength. The results indicated that the bonding performance and the wettability of high R value blending modification were superior to that of low R value case. In addition, the optimal bonding performance came from the MUF resin modified by 15% BPUP (R = 5) addition. Besides, the K value on wood substrates with different moisture contents (MC) was calculated by wetting model to interpret the wetting kinetics. The polymer blending adhesive has a potential capacity for making wood-based panels from high-moisture raw materials.
引用
收藏
页码：185 / 191
页数：6
相关论文
共 57 条
[1]  
Cai X(2010)A study on the curing and viscoelastic characteristics of melamine–urea–formaldehyde resin in the presence of aluminium silicate nanoclays Compos A Appl Sci Manuf 41 604-611
[2]  
Riedl B(1972)Measuring the wetting of wood surfaces by adhesives Jpn Wood Res Soc J 18 451-456
[3]  
Wan H(1999)Synthesis and properties of thermotropic liquid crystalline polyurethane elastomers (II): effect of structure of chain extender containing imide unit Korea Polym J 7 356-363
[4]  
Zhang SY(1994)Analysis of the wood-wetting process Holzforschung 48 139-144
[5]  
Wang XM(1995)A model for the description of polymer surface dynamic behavior 1: contact angle vs polymer surface properties Langmuir 11 2674-2681
[6]  
Chen CM(2006)Surface characterization of chemically modified wood: dynamic wettability Wood Fiber Sci 38 497-511
[7]  
Lee DJ(2006)Improved water resistance and adhesive performance of a commercial UF resin blended with glutaraldehyde J Adhes 82 629-641
[8]  
You SH(2007)Glutaraldehyde-modified MUF adhesive system–Improved hot water resistance Holz Roh-Werkst 65 251-253
[9]  
Kim HD(2005)Demonstration of co-polymerization in melamine–urea–formaldehyde reactions using 15 Polymer 46 2153-2156
[10]  
Liptáková E(2003) NMR correlation spectroscopy Eur J Wood Prod 61 77-78
123456