Unveiling the role of trivalent cation incorporation in Li-rich Mn-based layered cathode materials for low-cost lithium-ion batteries

被引：0
作者：
Moustafa M. S. Sanad
Arafat Toghan
机构：
[1] Central Metallurgical Research and Development Institute,Chemistry Department, Faculty of Science
[2] South Valley University,Chemistry Department, College of Science
[3] Imam Mohammad Ibn Saud Islamic University (IMSIU),undefined
来源：
Applied Physics A | 2021年 / 127卷
关键词：
Layered materials; Structural properties; Electronic conductivity; Lithium-ion batteries;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A simple solvothermal route was successfully implemented for fabrication of Li-rich Mn-based layered cathode Li1.15Ni0.15Co0.15Mn0.7M0.01O2 (LMLC) materials through incorporation of different trivalent cations (M3+: Al3+, Cr3+ or Fe3+). The structural properties of mixed solid solution of rhombohedral LiNiO2 phase and monoclinic Li2MnO3 phases were checked by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). LMLC-Fe sample shows the highest coercivity Hc value of about 198.1 Oe, and the lowest dielectric constant εr about 74. LMLC-Cr sample exhibits the lowest activation energy (Ea = 0.163 eV) for electric conduction as a result of the smallest cell volume and particle size. LMLC-Al electrode material delivers the highest initial charge and discharge capacity of about 140 and 104 mAh/g at 0.1 C, respectively maintaining around 70% of the initial capacity at 0.1C. Both LMLC-Al and LMLC-Cr samples show better high rate capabilities than that of LMLC-Fe sample.
引用
收藏
相关论文
共 351 条
[51]  
Song Y(2007)Review of the U.S. Department of Energy's "deep dive" to understand voltage fade in Li- and Mn-rich cathodes Chem. Mater. 5 27375-1388
[52]  
Zou G(2015)Electrochemical properties of MgO-coated 0.5 Li2MnO3–0.5 LiNi0.5Mn0.5O2 composite cathode material for lithium ion battery RSC Adv. 3 743-282
[53]  
Hu L(2015)Effect of FePO4 coating on performance of Li Ener. Technol. 56 13051-A94
[54]  
Yi L(2017)Mn Inorg. Chem. 34 404-1060
[55]  
Yu HJ(2016)Ni Mater. Sci-Pol. 11 258-125
[56]  
Zhou HS(2017)Co Process. Appl. Ceram. 7 1379-3605
[57]  
Dong X(2017)O Results Phys. 95 275-C105
[58]  
Xu YL(1997) as cathode material for Li-ion battery Solid State Ionics 5 A92-1060
[59]  
Yan S(2002)Improvement of cycling performance in Ti substituted 0.5Li2MnO3–0.5LiNi0.5Mn0.5O2 through suppressing metal dissolution Electrochem. Solid-State Lett. 57 1057-980
[60]  
Mao SC(1996)Synthesis and electrochemical study of Zr-doped Li[Li J. Phys. Chem. Solids 68 120-undefined
12345678910