Corrosion Behavior of Weathering Steel Under Thin Electrolyte Layer at Different Relative Humidity

被引：0
作者：
Yan Xia
Pan Liu
Jianqing Zhang
Fahe Cao
机构：
[1] Zhejiang University,China State Key Laboratory of Silicon Materials, Key Laboratory of Advanced Materials and Applications for Batteries of Zhejiang Province, School of Materials Science and Engineering
[2] Zhejiang University,Department of Chemistry
来源：
Journal of Materials Engineering and Performance | 2018年 / 27卷
关键词：
EIS; electrochemical noise; relative humidity; thin electrolyte layer; weathering steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion behavior of weathering steel under thin electrolyte layer (TEL) at different relative humidity (RH) was investigated by cathodic polarization, electrochemical impedance spectroscopy, electrochemical noise, SEM/EDS, XRD and Raman spectroscopy. The results indicate that during the initial stage, the corrosion rate increases as the RH decreases when the initial thickness of TEL is above 100 μm. During the middle and final corrosion stages, the corrosion behavior of weathering steel is influenced by RH, the initial thickness of TEL and corrosion product. The TEL corrosion is divided into three types, and a weathering steel corrosion model under TEL and bulk solution is also proposed.
引用
收藏
页码：202 / 218
页数：16
相关论文
共 50 条
[31]   Corrosion of Stirrups under Different Relative Humidity Conditions in Concrete Exposed to Chloride Environment [J].
Gu, Xiang-Lin ;
Dong, Zheng ;
Yuan, Qin ;
Zhang, Wei-Ping .
JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2020, 32 (01)
[32]   Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition [J].
Thee, Ch. ;
Hao, Long ;
Dong, Junhua ;
Mu, Xin ;
Wei, Xin ;
Li, Xiaofang ;
Ke, Wei .
CORROSION SCIENCE, 2014, 78 :130-137
[33]   Investigation on Electrochemical Corrosion of 304 Stainless Steel under Thin Electrolyte Layers Containing Chloride Ions [J].
Cheng, Xuequn ;
Luo, Hong ;
Xiao, Kui ;
Dong, Chaofang .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2017, 12 (09) :8006-8020
[34]   Effect of sea salt and relative humidity on corrosion rate of carbon steel in humidity test [J].
Oshikawa W. ;
Yamada M. ;
Nakano A. .
Zairyo to Kankyo/ Corrosion Engineering, 2010, 59 (10) :390-392
[35]   Modelling of galvanic corrosion based on potentiodynamic polarisation measurements under a thin layer of electrolyte [J].
Jenicek, Vit ;
Diblikova, Linda ;
Pazderova, Martina .
MATERIAUX & TECHNIQUES, 2015, 103 (05)
[36]   Corrosion Behavior of Weathering Test Steel for Bridge Under the Neutral Wet/Dry Alternate Condition [J].
XU Xiao-lian .
Journal of Iron and Steel Research(International), 2011, 18 (S1) :951-955
[37]   Corrosion Behavior of Weathering Test Steel for Bridge Under the Neutral Wet/Dry Alternate Condition [J].
Xu Xiao-lian ;
Zhong Bin ;
Ai Fang-fang ;
Chen Yi-qing ;
Xiao Yu ;
Li Lin .
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2011, 18 :951-955
[38]   Effects of electrolyte thickness, chloride ion concentration, and an external direct current electric field on corrosion behaviour of silver under a thin electrolyte layer [J].
Bu, F. R. ;
Li, J. N. ;
Huang, H. L. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2019, 54 (02) :143-153
[39]   Evolution of rust layers on carbon steel and weathering steel in high humidity and heat marine atmospheric corrosion [J].
Yueming Fan ;
Wei Liu ;
Shimin Li ;
Thee Chowwanonthapunya ;
Banthukul Wongpat ;
Yonggang Zhao ;
Baojun Dong ;
Tianyi Zhang ;
Xiaogang Li .
JournalofMaterialsScience&Technology, 2020, 39 (04) :190-199
[40]   Corrosion current distributions in a low-alloy steel covered with a layer of rust formed under electrolyte thin films in a NaCl solution [J].
Yamashita, M ;
Yonezawa, T ;
Uchida, H .
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1999, 63 (10) :1332-1337
12345