Corrosion Behavior of Weathering Steel Under Thin Electrolyte Layer at Different Relative Humidity

被引：0
作者：
Yan Xia
Pan Liu
Jianqing Zhang
Fahe Cao
机构：
[1] Zhejiang University,China State Key Laboratory of Silicon Materials, Key Laboratory of Advanced Materials and Applications for Batteries of Zhejiang Province, School of Materials Science and Engineering
[2] Zhejiang University,Department of Chemistry
来源：
Journal of Materials Engineering and Performance | 2018年 / 27卷
关键词：
EIS; electrochemical noise; relative humidity; thin electrolyte layer; weathering steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion behavior of weathering steel under thin electrolyte layer (TEL) at different relative humidity (RH) was investigated by cathodic polarization, electrochemical impedance spectroscopy, electrochemical noise, SEM/EDS, XRD and Raman spectroscopy. The results indicate that during the initial stage, the corrosion rate increases as the RH decreases when the initial thickness of TEL is above 100 μm. During the middle and final corrosion stages, the corrosion behavior of weathering steel is influenced by RH, the initial thickness of TEL and corrosion product. The TEL corrosion is divided into three types, and a weathering steel corrosion model under TEL and bulk solution is also proposed.
引用
收藏
页码：202 / 218
页数：16
相关论文
共 50 条
[21]   Influence mechanism of Ni content on corrosion behavior of weathering steel under the simulated industrial atmosphere [J].
Liu, Weiming ;
Bian, Qingsong ;
Liao, Jun ;
Wang, Qiyu ;
Pan, Hongbo ;
Cao, Fabin ;
Wu, Zhaojin .
JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2025,
[22]   Rust layer adhesion capability and corrosion behavior of weathering steel under tension during initial stages of simulated marine atmospheric corrosion [J].
Guo, Xiaoyu ;
Zhu, Jinsong ;
Kang, Jingfu ;
Duan, Menghao ;
Wang, Yongguang .
CONSTRUCTION AND BUILDING MATERIALS, 2020, 234
[23]   Effect of Hydrogen Charging on the Stress Corrosion Behavior of 2205 Duplex Stainless Steel Under 3.5 wt.% NaCl Thin Electrolyte Layer [J].
Zhao, Tianliang ;
Liu, Zhiyong ;
Hu, Shanshan ;
Du, Cuiwei ;
Li, Xiaogang .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (06) :2837-2846
[24]   Effect of Hydrogen Charging on the Stress Corrosion Behavior of 2205 Duplex Stainless Steel Under 3.5 wt.% NaCl Thin Electrolyte Layer [J].
Tianliang Zhao ;
Zhiyong Liu ;
Shanshan Hu ;
Cuiwei Du ;
Xiaogang Li .
Journal of Materials Engineering and Performance, 2017, 26 :2837-2846
[25]   Atmospheric Corrosion Behavior of Weathering Steel in Periodically Changed Environment [J].
Zhang, Xu ;
Yang, Shanwu ;
Guo, Hui ;
He, Xinlai .
ISIJ INTERNATIONAL, 2014, 54 (04) :909-915
[26]   Corrosion behavior of weathering steel in marine atmosphere [J].
Zhang, QC ;
Wu, JS ;
Wang, JJ ;
Zheng, WL ;
Chen, JG ;
Li, AB .
MATERIALS CHEMISTRY AND PHYSICS, 2003, 77 (02) :603-608
[27]   The influence of different locations on copper corrosion with different external electric fields under a chloride-containing thin electrolyte layer [J].
Huang, Hualiang ;
Bu, Furong .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2019, 54 (03) :257-265
[28]   Effect of Ni on the oxidation behavior of corrosion products that form on low alloy steel exposed to a thin electrolyte layer environment [J].
Jiang, Shan ;
Cao, Jian-ping ;
Liu, Zhi-yong ;
Xu, Xue-xu ;
Yang, Jian-wei ;
Li, Xue-tao .
CORROSION SCIENCE, 2022, 206
[29]   Corrosion of pure magnesium under thin electrolyte layers [J].
Zhang, Tao ;
Chen, Chongmu ;
Shao, Yawei ;
Meng, Guozhe ;
Wang, Fuhui ;
Li, Xiaogang ;
Dong, Chaofang .
ELECTROCHIMICA ACTA, 2008, 53 (27) :7921-7931
[30]   Corrosion behaviour of copper under chloride-containing thin electrolyte layer [J].
Liao, Xiaoning ;
Cao, Fahe ;
Zheng, Liyun ;
Liu, Wenjuan ;
Chen, Anna ;
Zhang, Jianqing ;
Cao, Chunan .
CORROSION SCIENCE, 2011, 53 (10) :3289-3298
12345