Kinetics and Thermodynamics of Sorption for As(V) on the Porous Biomorph-Genetic Composite of α-Fe2O3/Fe3O4/C with Eucalyptus Wood Hierarchical Microstructure

A novel porous biomorph-genetic composite of α-Fe2O3/Fe3O4/C (PBGC-Fe/C) with eucalyptus wood template was prepared, characterized and tested for its sorption capacity of As(V) from aqueous solution. The result indicated that the PBGC-Fe/C material retained the hierarchical porous structure of eucalyptus wood with three different types of pores (widths 70∼120, 4.1∼6.4 and 0.1∼1.3 μm) originating from vessels, fibres and pits of the wood, respectively. Its surface area was measured to be 59.2 m2/g. With increasing initial As(V) concentration from 5 to 100 mg/L, the amounts of As(V) sorbed on the pulverized PBGC-Fe/C sorbent (<0.149 mm) increased from 0.50 to 4.01 mg/g at 25 °C, from 0.50 to 4.83 mg/g at 35 °C and from 0.50 to 4.19 mg/g at 45 °C, and the corresponding removal rates decreased from 99.97 to 40.10 % at 25 °C, 99.95 to 48.40 % at 35 °C and 99.92 to 42.05 % at 45 °C. At the initial concentrations of 5, 10 and 50 mg/L, the sorption capacities for the unpulverized PBGC-Fe/C sorbent (>3 mm) were determined to be 0.50, 0.99 and 2.49 mg/g, respectively, which exhibited a similar average value to those of fine particles or nanoparticles of iron oxides. The sorption could well be described by the pseudo-second-order kinetic equation. The equilibrium data were found to follow Freundlich as well as Langmuir isotherms.