Dielectric properties of Erbium doped CaCu3Ti4O12 prepared by sol–gel self combustion method

The dielectric properties of Erbium doped CaCu3Ti(4–x)ErxO(12–δ) with x = 0, 0.05, 0.1 were synthesized by the sol–gel self combustion method. XRD (X-ray powder diffraction) analysis confirmed the formation of single-phase material in the samples calcined at 800 °C. Crystal structure does not change on doping with Erbium and it remains cubic in all the three compositions studied. It is found that lattice parameter increases slightly with Erbium doping. The surface morphology of CaCu3Ti(4–x)ErxO(12–δ) powders sintered at 950 °C in air for 3 h was observed using high resolution—scanning electron microscope and it shows that the grain size is in the range of 1–8 μm for these samples. Energy dispersive X-ray spectroscopy pattern confirmed the presence of Erbium with 1.9 and 4.86 atomic percentages with doping concentration. The dielectric characteristics of CaCu3Ti(4–x)ErxO(12–δ) were studied by LCR meter in the frequency range (100 Hz–1 MHz) at various temperatures (RT to 500 °C). Interestingly, the dielectric constant increases and dielectric loss had lower values than those of undoped CCTO.