High crystal quality wurtzite-zinc blende heterostructures in metal-organic vapor phase epitaxy-grown GaAs nanowires

We have prepared GaAs wurtzite (WZ)-zinc blende (ZB) nanowire heterostructures by Au particle-assisted metal-organic vapor phase epitaxy (MOVPE) growth. Superior crystal quality of both the transition region between WZ and ZB and of the individual segments themselves was found for WZ-ZB single heterostructures. Pure crystal phases were achieved and the ZB segments were found to be free of any stacking defects, whereas the WZ sections showed a maximum stacking fault density of 20 μm−1. The hexagonal cross-sectional wires are terminated by \documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$$\left\{ {10\bar 10} \right\}$$\end{document}-type side facets for the WZ segment and predominantly {110}-type side facets for the ZB part of the wire. A diameter increase occurred after the transition from WZ to ZB. Additionally, facets of the \documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$$\left\{ {\bar 1\bar 1\bar 1} \right\}$$\end{document}-type as well as downwards-directed overgrowth of the WZ segments were formed at the WZ to ZB transition to compensate for the observed diameter increase and facet rotation. In the case of WZ-ZB multiple heterostructures, we observed slightly higher densities of stacking faults and twin planes compared to single heterostructures. [graphic not available: see fulltext]