Fabrication and adsorption properties of hybrid material with micropores from SBA-15

被引：0
作者：
Tiantian Li
Yuan Yuan
Yingqiao Xiang
Annan Zhou
Qinghong Xu
机构：
[1] Beijing University of Chemical Technology,State Key Laboratory of Chemical Resource Engineering
[2] PetroChina Company Limited,Petrochemical Research Institute
来源：
Chemical Research in Chinese Universities | 2016年 / 32卷
关键词：
Fabrication; Mesopore; Micropore; NaCl; Adsorption;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A novel hybrid material with microporous structure was fabricated from SBA-15 with mesopores via silane modification and hydrolysis. Two kinds of pores with diameters of 6.5 and 1.9 nm were found in the hybrid material. Compared to that of SBA-15, the surface area of the hybrid material increased from 395.9 m2/g to 667.4 m2/g while its porous volume decreased. The new hybrid material was found to have high efficiency in removing NaCl from solution, and the maximum adsorption capacity of it was ca. 517.5 mg/g.
引用
收藏
页码：334 / 337
页数：3
相关论文
共 157 条
[1]  
Li W. J.(2015)undefined Catalysis Today 251 53-undefined
[2]  
Ye L. M.(2013)undefined J. Mater. Chem. A 1 9351-undefined
[3]  
Chen J.(2013)undefined Nano Lett. 13 4182-undefined
[4]  
Yuan Y. Z.(2013)undefined Chem. Soc. Rev. 42 6593-undefined
[5]  
Figueiredo J. L.(2015)undefined Chem. Res. Chinese Universities 31 138-undefined
[6]  
Lei Y.(2015)undefined Chem. Eng. J. 273 630-undefined
[7]  
Lu J.(2014)undefined Org. Process Res. Dev. 18 257-undefined
[8]  
Lu X. Y.(2015)undefined J. Colloid Interface Sci. 454 134-undefined
[9]  
Amine K.(2015)undefined Microelectron. Eng. 133 1-undefined
[10]  
Li X. H.(2012)undefined Biomaterials 33 1428-undefined
12345678910