Long-term durability of onshore coated concrete —chloride ion and carbonation effects

被引：0

作者：

Seyedhamed Sadati

Mehdi K. Moradllo

Mohammad Shekarchi

机构：

[1] Missouri University of Science and Technology,Civil, Architectural, and Environmental Engineering Department

[2] Oklahoma State University,Department of Civil Engineering, 207 Engineering South

[3] University of Tehran,College of Engineering, School of Civil Engineering, Construction Materials Institute (CMI)

来源：

Frontiers of Structural and Civil Engineering | 2016年 / 10卷

关键词：

carbonation; chloride ion; corrosion; service life; surface coating;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Enhancing service life of reinforced concrete (RC) structures located in marine environments is an issue of great interest for design engineers. The present research addresses the effect of surface coatings on service life of onshore RC structures. Long-term performance of concrete samples up to 88 months of exposure at natural marine environment was investigated. Two onshore exposure conditions, including soil and atmosphere and different types of concrete coatings were studied. Carbonation rates of up to 0.5 and 1.5 mm/year were observed at the first 88 months of exposure for soil and atmospheric samples, respectively. Surface chloride ion build-up and variation in chloride ion diffusion were monitored with respect to time, and service life was estimated. Based on the obtained results it is proposed to use the aliphatic acrylic and polyurethane coatings for enhancing the service life of concrete structures in the investigated exposure conditions.

引用

页码：150 / 161

页数：11

共 50 条

[41] Long-term chloride-induced corrosion monitoring of reinforced concrete coated with commercial polymer-modified mortar and polymeric coatings
Brenna, A.
Bolzoni, F.
Beretta, S.
Ormellese, M.
CONSTRUCTION AND BUILDING MATERIALS, 2013, 48 : 734 - 744
[42] Long-term mechanical and durability properties of recycled aggregate concrete prepared with the incorporation of fly ash
Kou, Shi-Cong
Poon, Chi-Sun
CEMENT & CONCRETE COMPOSITES, 2013, 37 : 12 - 19
[43] Long term effect of strength and durability performance of concrete containing sulphate reduction bacteria under chloride condition
Irwan, J. M.
Teddy, T.
Othman, N.
Khalid, F. S.
2ND GLOBAL CONGRESS ON CONSTRUCTION, MATERIAL AND STRUCTURAL ENGINEERING, 2020, 713
[44] Study on Durability of Concrete with Machine-made Sand Part II: Long-term Carbonization
Zhao, Shunbo
Li, Yutao
Xu, Yangyang
CIVIL ENGINEERING, ARCHITECTURE AND SUSTAINABLE INFRASTRUCTURE II, PTS 1 AND 2, 2013, 438-439 : 10 - 14
[45] Macroscopic observations on the long-term effects of cathodic protection applied to carbonated reinforced concrete
Redaelli, E.
Bertolini, L.
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (08): : 756 - 762
[46] Compressive Strength, Chloride Ion Penetrability, and Carbonation Characteristic of Concrete with Mixed Slag Aggregate
Choi, Se-Jin
Kim, Young-Uk
Oh, Tae-Gue
Cho, Bong-Suk
MATERIALS, 2020, 13 (04)
[47] Evaluation of the long-term performance and durability of basalt fiber reinforced polymer bars in concrete structures
Su, Chang
Wang, Xin
Ding, Lining
Peng, Zheqi
Zhou, Jingyang
Chen, Zhiyuan
Liu, Shui
Wu, Zhishen
CONSTRUCTION AND BUILDING MATERIALS, 2024, 448
[48] Characterization of Steel/Concrete Interface For a Long-Term Corroded Beam Stored in Chloride Environment
Zhang, Ruijin
Yang, Huilin
L'Hostis, Valerie
Castel, Arnaud
Francois, Raoul
ADVANCES IN STRUCTURES, PTS 1-5, 2011, 163-167 : 3415 - 3420
[49] Study on the bond behavior of steel bars embedded in concrete under the long-term coupling of repeated loads and chloride ion erosion
Shang, Huaishuai
Yang, Jiaxing
Huang, Yue
Fan, Liang
Wang, Randuo
CONSTRUCTION AND BUILDING MATERIALS, 2022, 323
[50] Microstructure and chloride transport of aeolian sand concrete under long-term natural immersion
Dong, Wei
Sun, AnQi
Zhou, Menghu
SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 2024, 31 (01)

← 1 2 3 4 5 →