Phase Equilibria in the Ternary Al–Ti–Pt System. I. Solidus Surface of the Al–Ti–Pt System in the Range 0–50 at.% Pt

被引：0
|
作者：
O. V. Zaikina
V. G. Khoruzhaya
K. Ye. Korniyenko
K. A. Meleshevich
D. V. Pavlyuchkov
T. Ya. Velikanova
机构：
[1] National Academy of Sciences of Ukraine,Frantsevich Institute for Problems of Materials Science
来源：
Powder Metallurgy and Metal Ceramics | 2019年 / 57卷
关键词：
phase equilibria; solidus surface; isothermal plane; ternary compound; structural type; solid solution;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The nature of phase equilibria has been examined for the first time in the Al–Ti–Pt system in the range 0–50 at.% Pt at subsolidus temperatures. Besides the τ1, τ2, and τ3 ternary compounds with AuCu3, Th6Mn23+1, and MgZn2 lattices known from the literature, eight more compounds form in the system at subsolidus temperatures. The structural type is known for three of these compounds. They are τ4 (ZrBeSi), τ5 (CrFe), and τ6 (defective structure of Au4Al type). There are 31 isothermal planes on the solidus surface. All planes are formed with participation of ternary compounds and solid solutions based on binary compounds present in the boundary systems. The highest temperature in this composition range corresponds to the congruent melting of the TiPt phase (1830°C) and the lowest to eutectic l ⇄ <Al> + <Al21Pt5> in the binary Al–Pt system (655°C).
引用
收藏
页码：587 / 595
页数：8
相关论文
共 50 条
  • [1] Phase Equilibria in the Ternary Al-Ti-Pt System. I. Solidus Surface of the Al-Ti-Pt System in the Range 0-50 at.% Pt
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Meleshevich, K. A.
    Pavlyuchkov, D. V.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (9-10) : 587 - 595
  • [2] Phase Equilibria in the Ternary Al–Ti–Pt System. II. Liquidus Surface of the Al–Ti–Pt System in the Compositions Range 0–50 at.% Pt
    O. V. Zaikina
    V. G. Khoruzhaya
    K. Ye. Korniyenko
    D. V. Pavlyuchkov
    K. A. Meleshevich
    T. Ya. Velikanova
    Powder Metallurgy and Metal Ceramics, 2019, 57 : 709 - 715
  • [3] Phase Equilibria in the Ternary Al–Ti–Pt System. IV. Vertical Sections in the Ternary Al–Ti–Pt System in the Composition Range 0–50 at.% Pt
    V. G. Khoruzhaya
    K. Ye. Korniyenko
    Powder Metallurgy and Metal Ceramics, 2019, 58 : 323 - 328
  • [4] Phase Equilibria in the Ternary Al–Ti–Pt System. III. The Al–Ti–Pt Melting Diagram in the Composition Range 0–50 at.% Pt
    O. V. Zaikina
    V. G. Khoruzhaya
    K. Ye. Korniyenko
    T. Ya. Velikanova
    Powder Metallurgy and Metal Ceramics, 2019, 58 : 81 - 88
  • [5] Phase Equilibria in the Ternary Al-Ti-Pt System. II. Liquidus Surface of the Al-Ti-Pt System in the Compositions Range 0-50 at.% Pt
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Pavlyuchkov, D. V.
    Meleshevich, K. A.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (11-12) : 709 - 715
  • [6] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-Pt SYSTEM. IV. VERTICAL SECTIONS IN THE TERNARY Al-Ti-Pt SYSTEM IN THE COMPOSITION RANGE 0-50 at.% Pt
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (5-6) : 323 - 328
  • [7] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-PT SYSTEM. III. THE Al-Ti-PT MELTING DIAGRAM IN THE COMPOSITION RANGE 0-50 at.% PT
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (1-2) : 81 - 88
  • [8] The Constitution of Alloys and Phase Diagram of the Ternary Al–Cr–Pt System at 50–100 at.% Pt. I. Solidus Surface and Isothermal Section in the Al–Cr–Pt System at 1350 C in the Range 50–100 at.% Pt
    K. E. Kornienko
    V. G. Khoruzha
    K. A. Meleshevich
    M. V. Karpets
    Powder Metallurgy and Metal Ceramics, 2013, 52 : 314 - 328
  • [9] The Constitution of Alloys and Phase Diagram of the Ternary Al-Cr-Pt System at 50-100 at.% Pt. I. Solidus Surface and Isothermal Section in the Al-Cr-Pt System at 1350 C in the Range 50-100 at.% Pt
    Kornienko, K. E.
    Khoruzha, V. G.
    Meleshevich, K. A.
    Karpets, M. V.
    POWDER METALLURGY AND METAL CERAMICS, 2013, 52 (5-6) : 314 - 328
  • [10] Phase Equilibria in the Aluminum Corner of the Al–Ti–Pt System
    O. V. Zaikina
    V. G. Khoruzha
    K. E. Kornienko
    T. Ya. Velikanova
    Powder Metallurgy and Metal Ceramics, 2018, 57 : 114 - 126
12345