Tensile Properties Variation Across the Dissimilar Metal Weld Joint Between Modified 9Cr–1Mo Ferritic Steel and 316LN Stainless Steel at RT and 550 °C

被引:12
作者
Karthick K. [1 ]
Malarvizhi S. [1 ]
Balasubramanian V. [1 ]
Gourav Rao A. [2 ]
机构
[1] Department of Manufacturing Engineering, Centre for Materials Joining and Research (CEMAJOR), Annamalai University, Annamalai Nagar, 608 002, Tamil Nadu
[2] Naval Materials Research Laboratory (NMRL), Ambernath, Maharashtra
关键词
Dissimilar metal weld joint; Microhardness; Microstructures; P91-ferritic steel; SS 316LN stainless steel; Tensile properties;
D O I
10.1007/s13632-018-0430-9
中图分类号
学科分类号
摘要
In liquid metal cooled fast breeder reactors (LMFBR), modified 9Cr–1Mo ferritic steel (P91 or Grade 91) is a preferred material for constructing steam generators due to its creep strength and stress corrosion cracking resistance. The austenitic stainless steels (SS 316LN and SS 304LN) are widely used for primary and secondary piping systems because of its oxidation resistance and excellent creep strength. So, the dissimilar metal weld joint (DMWJ) between P91 and SS 316LN is inevitable. Nickel-based consumables (Alloy 82 and Alloy 182) are preferred to join these materials. The DMWJ will experience the temperature up to 550 °C. For accurate integrity assessment, the mechanical properties of individual regions are to be evaluated at room temperature (RT) and 550 °C. Hence, the present investigation is focused on evaluating the mechanical properties of various regions of DMWJ at RT and 550 °C. From this investigation, it is understood that the tensile properties are heterogeneous across the DMWJ at RT and 550 °C. The high-temperature (550 °C) tensile properties are significantly lower with respect to the RT properties. The development of complex microstructures at the interfaces will alter the mechanical properties across the DMWJ. © 2018, Springer Science+Business Media, LLC, part of Springer Nature and ASM International.
引用
收藏
页码:209 / 221
页数:12
相关论文
共 35 条
[1]  
Kumar P., Pai A., An overview of welding aspects and challenges during manufacture of intermediate heat exchangers for 500 MWe prototype fast breeder reactor, Proc. Eng., 86, Ic, pp. 173-183, (2014)
[2]  
Puthiyavinayagam P., Selvaraj P., Balasubramaniyan V., Raghupathy S., Velusamy K., Devan K., Et al., Development of fast breeder reactor technology in India, Prog. Nucl. Energy, (2017)
[3]  
Swindeman R.W., Santella M.L., Maziasz P.J., Roberts B.W., Coleman K., Issues in replacing Cr–Mo steels and stainless steels with 9Cr–1Mo–V steel, Int. J. Press. Vessels Pip., 81, 6, pp. 507-512, (2004)
[4]  
Velusamy K., Chellapandi P., Chetal S.C., Raj B., Overview of pool hydraulic design of Indian prototype fast breeder reactor, Sadhana—Acad. Proc. Eng. Sci., 35, 2, pp. 97-128, (2010)
[5]  
Bhaduri A.K., Venkadesan S., Rodriguez P., Mukunda P.G., Transition metal joints for steam generators—an overview, Int. J. Press. Vessels Pip., 58, 3, pp. 251-265, (1994)
[6]  
Sarikka T., Ahonen M., Mouginot R., Nevasmaa P., Karjalainen-Roikonen P., Ehrnsten U., Hanninen H., Microstructural, mechanical, and fracture mechanical characterization of SA 508-alloy 182 dissimilar metal weld in view of mismatch state, Int. J. Press. Vessel. Pip., 145, pp. 13-22, (2016)
[7]  
Kumar S., Singh P.K., Karn K.N., Bhasin V., Experimental investigation of local tensile and fracture resistance behaviour of dissimilar metal weld joint: SA508 Gr.3 Cl.1 and SA312 type 304LN, Fatigue Fract. Eng. Mater. Struct., 40, pp. 190-206, (2017)
[8]  
Wang H.T., Wang G.Z., Xuan F.Z., Liu C.J., Tu S.T., Local mechanical properties of a dissimilar metal welded joint in nuclear powersystems, Mater. Sci. Eng. A, 568, pp. 108-117, (2013)
[9]  
Rathod D.W., Pandey S., Singh P.K., Prasad R., Mechanical properties variations and comparative analysis of dissimilar metal pipe welds in pressure vessel system of nuclear plants, J. Pressure Vessel Technol., 138, 1, (2015)
[10]  
Kim J.W., Lee K., Kim J.S., Byun T.S., Local mechanical properties of alloy 82/182 dissimilar weld joint between SA508 Gr.1a and F316 SS at RT and 320 °C, J. Nucl. Mater., 384, 3, pp. 212-221, (2009)