Effect of Hot Isostatic Pressing on the Structure and Properties of Articles from Alloy VT6 Obtained by Cold Gas-Dynamic Spraying

被引：0
作者：
A. A. Spasenko
V. V. Cheverikin
P. V. Petrovskii
机构：
[1] NITU “MISiS”,
来源：
Metal Science and Heat Treatment | 2021年 / 63卷
关键词：
additive technologies; cold gas dynamic spraying; porosity; titanium alloys; mechanical properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Samples of titanium alloy VT6 obtained by the method of cold gas dynamic spraying (CGDS) and subjected to hot isostatic pressing (HIP) for lowering the porosity and improving the mechanical properties are studied. The HIP is conducted at a temperature of 900°C and a pressure of 110 MPa. This reduces the volume fraction of pores from 8 to 0.5% and raises the ultimate strength of the samples from 70 to 950 MPa and the elongation by 12%.
引用
收藏
页码：86 / 90
页数：4
相关论文
共 22 条
  • [1] Assadi H(2003)Bonding mechanism in cold gas spraying Acta Mater. 51 4379-4394
  • [2] Gärtner F(2019)Comment of adiabatic shear instability is not necessary for adhesion in cold spray Scr. Mater. 162 512-514
  • [3] Stotenhoff T(2018)Adiabatic shear instability is not necessary for adhesion in cold spray Acta Mater. 158 430-439
  • [4] Kreye H(2015)Microstructure and mechanical property of Ti and Ti6Al4V prepared by an in-situ shot peening assisted cold spraying Mater. Des. 85 527-533
  • [5] Assadi H(2006)New opportunities to use cold spray process for applying additive features to titanium alloys Metal Powder Rep. 61 30-37
  • [6] Gärtner F(2017)Cold gas dynamic spray additive manufacturing today: Deposit possibilities, technological solutions and viable applications Mater Des. 133 266-287
  • [7] Klassen T(undefined)undefined undefined undefined undefined-undefined
  • [8] Kreye H(undefined)undefined undefined undefined undefined-undefined
  • [9] Hassani-Gangaraj M(undefined)undefined undefined undefined undefined-undefined
  • [10] Veysset D(undefined)undefined undefined undefined undefined-undefined
123