Preparation of highly stable TiO2 sols and nanocrystalline TiO2 films via a low temperature sol–gel route

被引：2
作者：
Akash Katoch
Hohyeong Kim
Taejin Hwang
Sang Sub Kim
机构：
[1] Inha University,School of Materials Science and Engineering
[2] Korea Institute of Industrial Technology,Surface Technology and Heat Treatment R&D Division
来源：
Journal of Sol-Gel Science and Technology | 2012年 / 61卷
关键词：
Nanocrystalline TiO; film; Sol–gel; Low temperature deposition; Stable TiO; sol;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Highly stable TiO2 sols were prepared by adjusting the water-to-titanium molar ratio to ~4 in the process of hydrolysis and condensation of titanium isopropoxide in ethanol with HNO3. Particularly, long-term stable TiO2 sols were prepared without adding any chemical additives. Anatase TiO2 nanocrystallites with sizes of 3–5 nm in diameter were uniformly dispersed in the stable sol. Crystallized TiO2 films were successfully deposited on Si (100) using the stable sol via a dip-coating process with low temperature curing at as low as 100 °C. The synthesized TiO2 sols and films are promising for use in flexible or dye-sensitized solar cells.
引用
收藏
页码：77 / 82
页数：5
相关论文
共 50 条
[31]   Variation of structural and optical properties of sol-gel TiO2 thin films with catalyst concentration and calcination temperature [J].
Ahn, YU ;
Kim, EJ ;
Kim, HT ;
Hahn, SH .
MATERIALS LETTERS, 2003, 57 (30) :4660-4666
[32]   Electrodeposition and characterization of nanocrystalline cuprous oxide thin films on TiO2 films [J].
Tang, YW ;
Chen, ZG ;
Jia, ZJ ;
Zhang, LS ;
Li, JL .
MATERIALS LETTERS, 2005, 59 (04) :434-438
[33]   Preparation of nanocrystalline TiN film by direct nitridation of TiO2 film [J].
Jiang, HB ;
Gao, L ;
Li, JG .
JOURNAL OF INORGANIC MATERIALS, 2003, 18 (02) :495-499
[34]   A low-temperature process to synthesize rutile phase TiO2 and mixed phase TiO2 composites [J].
Zhang, Peilin ;
Yin, Shu ;
Sato, Tsugio .
MATERIALS RESEARCH BULLETIN, 2010, 45 (03) :275-278
[35]   Stable hydrosols for TiO2 coatings [J].
Alphonse, Pierre ;
Varghese, Aneesha ;
Tendero, Claire .
JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2010, 56 (03) :250-263
[36]   Sol-gel-processed TiO2/SiO2 films for electro-optic effect [J].
Hou, Alin ;
Shi, Dongcheng ;
Yi, Maobin ;
Yan, Zhaoxu ;
Zhang, Daming ;
Liu, Shaolin ;
Sun, Jie ;
Gao, Weinan ;
Liu, Hongfei .
NONLINEAR OPTICS: TECHNOLOGIES AND APPLICATIONS, 2008, 6839
[37]   Fe2O3 - TiO2 THIN FILMS PREPARED BY SOL-GEL METHOD [J].
Suciu, Ramona -Crina ;
Rosu, Marcela Corina ;
Silipas, Teofil Danut ;
Indrea, Emil ;
Popescu, Violeta ;
Popescu, George Liviu .
ENVIRONMENTAL ENGINEERING AND MANAGEMENT JOURNAL, 2011, 10 (02) :187-192
[38]   Influence of pH value of TiO2 sol on surface gloss of corresponding TiO2 film coated on ceramic tiles [J].
Dai, W. X. ;
Chen, X. ;
Li, E. ;
Wang, X. X. ;
Liu, P. ;
Fu, X. Z. .
SURFACE ENGINEERING, 2009, 25 (02) :106-110
[39]   Characterization and properties of anatase TiO2 film prepared via colloidal sol method under low temperature [J].
Xi-Song Zhou ;
Ling-Jia Li ;
Yuan-Hua Lin ;
Ce-Wen Nan .
Journal of Electroceramics, 2008, 21 :795-797
[40]   Electrochemical properties of nanoporous TiO2 films [J].
Miki, T ;
Nishizawa, K ;
Suzuki, K ;
Kato, K .
ELECTROCERAMICS IN JAPAN VIII, 2006, 301 :83-86
12345