Preparation of Fluorine-free MXene Ti3C2Tx and Its Electrical Properties

被引:0
作者
Ming Yan
Hao Zhang
Yuxiao Deng
Tianai Yang
Jiangtao Huang
Yu Zhu
机构
[1] Hubei University of Technology,College of Materials and Chemical Engineering
[2] Hubei University of Technology,Collaborative Innovation Center of Green Light
[3] Hubei University of Technology,Weight Materials and Processing
来源
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2023年 / 38卷
关键词
lewis acid; fluorine-free; MXene; electrical properties;
D O I
暂无
中图分类号
学科分类号
摘要
The fluorine-free MXene was prepared by Lewis acid salt etching of ternary layered ceramic MAX phase material. The structure of fluorine-free MXene was characterized by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The study finds that the layer spacing of fluorine-free MXene is approximately twice that of MXene etched by the liquid-phase method, compared to the conventional liquid-phase method. It also has greater capacitive properties. Therefore, the MXene prepared by this method shows a great potential for application in the field of capacitors.
引用
收藏
页码:304 / 307
页数:3
相关论文
共 30 条
[1]  
Naguib M(2012)Two-dimensional Transition Metal Carbides[J] ACS Nano 6 1 322-1 331
[2]  
Mashtalir O(2011)Two-dimensional Nanocrystals Produced Byexfoliation of Ti Advanced Materials 23 4 248-4 253
[3]  
Carle J(2014)AIC Nature 516 78-81
[4]  
Naguib M(2014)[J] Chemistry of Materials 26 2 374-2 381
[5]  
Kurtoglu M(2015)Conductive Two-dimensional Titanium Carbide ‘Clay’ with High Volumetric Capacitance[] Nature Materials 14 1 135-1 141
[6]  
Presser V(2017)Transparent Conductive Two-dimensional Titanium Carbide Epitaxial Thin Films[J] Journal of Materials Chemistry A 5 21 663-21 668
[7]  
Ghidiu M(2018)Large-area High-quality 2D Ultrathin Mo Angewandte Chemie International Edition 57 6 115-6 119
[8]  
Lukatskaya M R(2019)C Superconducting Crystals[J] Journal of the American Chemical Society 141 4 730-4 737
[9]  
Zhao M Q(2021)Electrochemical Etching of Ti Chem. Electro. Chem. 8 957-962
[10]  
Halim J(2020)A-IC to Ti ACS Nano 14 891-898