Mechanical activation of the reactive sintering of titanium carbide

This paper describes the mechanical alloying of Ti and C powders by intensive grinding in a planetary mill. The effect of milling conditions and initial composition on the compositional homogeneity and properties of powders and samples consolidated by hot-pressing was studied by x-ray diffraction, scanning electron microscopy, and surface area measurement. The diffraction patterns indicated that a powder mixture ground for 24 hours transforms to TiC after sintering for only one minute at 600°C under a pressure of 3 GPa.